Synthesis of superacid-functionalized mesoporous nanocages with tunable pore diameters and their application in the synthesis of coumarins.

Here we demonstrate for the first time the preparation of a triflic acid (TFA)-functionalized mesoporous nanocage with tunable pore diameters by the wet impregnation method. The obtained materials have been unambiguously characterized by XRD, N(2) adsorption, FTIR spectroscopy, and NH(3) temperature-programmed desorption (TPD). From the characterization results, it has been found that the TFA molecules are firmly anchored on the surface of the mesoporous supports without affecting their acidity. We also demonstrate the effect of the pore and cage diameter of the KIT-5 supports on the loading of TFA molecules inside the pore channels. It has been found that the total acidity of the materials increases with an increase in the TFA loading on the support, whereas the acidity of the materials decreases with an increase in the pore diameter of the support. The acidity of the TFA-functionalized mesoporous nanocages is much higher than that of the zeolites and metal-substituted mesoporous acidic catalysts. The TFA-functionalized materials have also been employed as the catalysts for the synthesis of 7-hydroxy-4-methylcoumarin by means of the Pechmann reaction under solvent-free conditions. It has been found that the catalytic activity of the TFA-functionalized KIT-5 is much higher than that of zeolites and metal-substituted mesoporous catalytic materials in the synthesis of coumarin derivatives. The stability of the catalyst is extremely good and can be reused several times without much loss of activity in the above reaction.

ESR and photoluminescence properties of Cu doped ZnS nanoparticles.

Nanoparticles of Zn1-xCuxS with Cu concentrations of x=0.0, 0.1, 0.2, 0.3 and 0.4 were prepared by a co-precipitation reaction method from homogeneous solutions of zinc and copper salts. Both the ZnS and ZnS:Cu nanoparticles excited at about 370 nm exhibits a broad green emission band peaking around 491 nm, which confirms the characteristic feature of Zn2+ as well as Cu2+ ions as luminescent centers in the lattice. The TEM micrographs showed spherical morphology for ZnS nanocrystals and the average size of the particles was estimated to be around 8.5 nm. At liquid nitrogen temperature, ESR signal characteristic of Cu2+ ions was observed in samples of all concentrations. ESR spectra analysis also indicated that Cu2+ ions enter the host lattice by replacing Zn2+ ions with distorted tetrahedral site symmetry.