Use of Hydrothermal Carbonization to Improve the Performance of Biowaste-Derived Hard Carbons in Sodium Ion-Batteries.

Over the last years, hard carbon (HC) has been the most promising anode material for sodium-ion batteries due to its low voltage plateau, low cost and sustainability. In this study, biomass waste (spent coffee grounds, sunflower seed shells and rose stems) was investigated as potential material for hard carbon preparation combining a two-step method consisting of on hydrothermal carbonization (HTC), to remove the inorganic impurities and increase the carbon content, and a subsequent pyrolysis process. The use of HTC as pretreatment prior to pyrolysis improves the specific capacity in all the materials compared to the ones directly pyrolyzed by more than 100 % at high C-rates. The obtained capacity ranging between 210 and 280 mAh g-1 at C/15 is similar to the values reported in literature for biomass-based hard carbons. Overall, HC obtained from sunflower seed shell performs better than that obtained from the other precursors with an initial Coulombic efficiency (ICE) of 76 % and capacities of 120 mAh g-1 during 1000 cycles at C with a high capacity retention of 86-93 %.

Morphological Evolution and Solid-Electrolyte Interphase Formation on LiNi0.6Mn0.2Co0.2O2 Cathodes Using Highly Concentrated Ionic Liquid Electrolytes.

Employing high-voltage Ni-rich cathodes in Li metal batteries (LMBs) requires stabilization of the electrode/electrolyte interfaces at both electrodes. A stable solid-electrolyte interphase (SEI) and suppression of active material pulverization remain the greatest challenges to achieving efficient long-term cycling. Herein, studies of NMC622 (1 mAh cm-2) cathodes were performed using highly concentrated N-methyl-N-propylpyrrolidinium bis(fluorosulfonyl)imide (C3mpyrFSI) 50 mol % lithium bis(fluorosulfonyl)imide (LiFSI) ionic liquid electrolyte (ILE). The resulting SEI formed at the cathode enabled promising cycling performance (98.13% capacity retention after 100 cycles), and a low degree of ion mixing and lattice expansion was observed, even at an elevated temperature of 50 °C. Fitting of acquired impedance spectra indicated that the SEI resistivity (RSEI) had a low and stable contribution to the internal resistivity of the system, whereas active material pulverization and secondary grain isolation significantly increased the charge transfer resistance (RCT) throughout cycling.

Water as an Effective Additive for High-Energy-Density Na Metal Batteries? Studies in a Superconcentrated Ionic Liquid Electrolyte.

The effect of water on the properties of superconcentrated sodium salt solutions in ionic liquids (ILs) was investigated to design electrolytes for sodium battery applications with water as an additive. Water was added to a 50 mol % solution of NaFSI [FSI=bis(fluorosulfonyl)imide] in the ionic liquid N-methyl-N-propylpyrrolidinium bis(fluorosulfonyl)imide (C3 mpyrFSI). Although the thermal properties (e.g., glass transition temperature) showed little dependence on the water content, the viscosity and, in particular, the ionic conductivity were strongly affected. The Na|Na symmetrical cell cycling performance was strongly dependent on the applied current density as well as on the water content. At higher current densities (1.0 mA cm-2 ) the polarization profiles showed a water dependence, suggesting that water was actively involved in the formation of an improved solid electrolyte interface layer (SEI) for high-water-content samples (1000-5000 ppm), resulting in improved long-term cycling stability. The initial impedance of cells cycled at 1.0 mA cm-2 (measured after 20 cycles) was elevated after water addition, and large polarizations occured for the "wet" samples. However, with further cycling the wet cells began to exhibit lower polarization and improved stability compared to the "dry" sample. The Na|NaFePO4 cell cycling performance was also demonstrated with minimal effect on the cell capacity, further highlighting the negligible activity of water in these electrolyte systems. In fact, reduced cell polarization and a more clearly defined charge profile were evident after water addition. The work shown here suggests that water may be used as a convenient and inexpensive additive for superconcentrated sodium IL electrolytes for improved device performance.

Impact of the Acid Treatment on Lignocellulosic Biomass Hard Carbon for Sodium-Ion Battery Anodes.

The investigation of phosphoric acid treatment on the performance of hard carbon from a typical lignocellulosic biomass waste (peanut shell) is herein reported. A strong correlation is discovered between the treatment time and the structural properties and electrochemical performance in sodium-ion batteries. Indeed, a prolonged acid treatment enables the use of lower temperatures, that is, lower energy consumption, for the carbonization step as well as improved high-rate performance (122 mAh g-1 at 10 C).

The mechanism of NaFePO4 (de)sodiation determined by in situ X-ray diffraction.

The reaction mechanism occurring during the (de)intercalation of sodium into the host olivine FePO4 structure is thoroughly analysed through a combination of structural and electrochemical methods. In situ XRD experiments have confirmed that the charge and discharge reaction mechanisms are different and have revealed the existence of a solid solution domain from 1 < x < 2/3 in Na(x)FePO4 upon charge. The second part of the charge proceeds through a 2-phase reaction between Na(2/3)FePO4 and FePO4 with strongly varying solubility limits. The strong cell mismatch between Na(2/3)FePO4 and FePO4 enhances the effects of the diffuse interface and therefore varying solubility limits are first observed here in micrometric materials.

Er(3+)-doped nanoparticles for optical detection of magnetic field.

A bright persistent photoluminescence has been observed in Er(3+)-doped nanoparticles prepared by selective dissolution of bulk oxyfluoride nano-glass-ceramics. A 2 orders of magnitude decrease of intensity of the (4)S(3/2)-->(4)I(15/2) green emission band of Er(3+) in these nanoparticles is observed in magnetic fields up to 50 T. This strong luminescence sensitivity to magnetic field can be used for localization and distant optical detection of magnetic field in nanovolumes with a field-resolution of 0.01 T.