Al-Al3Ni In Situ Composite Formation by Wire-Feed Electron-Beam Additive Manufacturing.

The regularities of microstructure formation in samples of multiphase composites obtained by additive electron beam manufacturing on the basis of aluminum alloy ER4043 and nickel superalloy Udimet-500 have been studied. The results of the structure study show that a multicomponent structure is formed in the samples with the presence of Cr23C6 carbides, solid solutions based on aluminum -Al or silicon -Si, eutectics along the boundaries of dendrites, intermetallic phases Al3Ni, AlNi3, Al75Co22Ni3, and Al5Co, as well as carbides of complex composition AlCCr, Al8SiC7, of a different morphology. The formation of a number of intermetallic phases present in local areas of the samples was also distinguished. A large amount of solid phases leads to the formation of a material with high hardness and low ductility. The fracture of composite specimens under tension and compression is brittle, without revealing the stage of plastic flow. Tensile strength values are significantly reduced from the initial 142-164 MPa to 55-123 MPa. In compression, the tensile strength values increase to 490-570 MPa and 905-1200 MPa with the introduction of 5% and 10% nickel superalloy, respectively. An increase in the hardness and compressive strength of the surface layers results in an increase in the wear resistance of the specimens and a decrease in the coefficient of friction.

Microstructure and Corrosion Resistance of AA4047/AA7075 Transition Zone Formed Using Electron Beam Wire-Feed Additive Manufacturing.

A gradient transition zone was obtained using electron beam deposition from AA4047 wire on AA7075 substrate and characterized for microstructures, tensile strength and corrosion resistance. The microstructure of the transition zone was composed of aluminum alloy grains, Al/Si eutectics and Fe-rich and Si-rich particles. Such a microstructure provided strength comparable to that of AA7075-T42 substrate but more intense corrosion due to the higher amount of anodic Mg2Si particles. The as-deposited AA4047 zone formed above the transition zone was composed of aluminum alloy dendrites and interdendritic Al/Si eutectics with low mechanical strength and high corrosion potential.