Preventing sintering of nanoclusters on graphene by radical adsorption.

Metal nanoclusters, supported on inert substrates, exhibiting well-defined shapes and sizes in a broad range of temperatures are a major object of desire in nanotechnology. Here, a technique is presented that improves the thermal stability of monodisperse and crystalline transition metal nanoclusters grown in a regular array on metal-supported graphene. To stabilize the clusters after growth under ultrahigh vacuum the system composed of the aggregates and the graphene/metal interface is exposed to radicals resulting from the dissociation of diatomic gases. As a model system we have used Pt as the metal element for cluster growth and the template consisting of the moiré pattern resulting from the lattice mismatch between graphene and the Ir(111) surface. The study has been performed for deuterium and oxygen radicals, which interact very differently with graphene. Our results reveal that after radical exposure the thermally activated motion of Pt nanoclusters to adjacent moiré cells and the subsequent sintering of neighbor aggregates are avoided, most pronounced for the case of atomic O. For the case of D the limits of the improvement are given by radical desorption, whereas for the case of O they are defined by an interplay between coalescence and graphene etching followed by Pt intercalation, which can be controlled by the amount of exposure. Finally, we determined the mechanism of how radical adsorption improves the thermal stability of the aggregates.

Oxygen orders differently under graphene: new superstructures on Ir(111).

Using scanning tunneling microscopy, the oxygen adsorbate superstructures on bare Ir(111) are identified and compared to the ones formed by intercalation in between graphene and the Ir(111) substrate. For bare Ir(111) we observe O-(2 × 2) and O-(2 × 1) structures, thereby clarifying a persistent uncertainty about the existence of these structures and the role of defects for their stability. For the case of graphene-covered Ir(111), oxygen intercalation superstructures can be imaged through the graphene monolayer by choosing proper tunneling conditions. Depending on the pressure, temperature and duration of O2 exposure as well as on the graphene morphology, O-(2 × 2), O-(√3×√3)-R30°, O-(2 × 1) and O-(2√3 × 2√3)-R30° superstructures with respect to Ir(111) are observed under the graphene cover. Two of these structures, the O-(√3 × âˆš3)-R30° and the (2√3 × 2√3)-R30° structure are only observed when the graphene layer is on top. Phase coexistence and formation conditions of the intercalation structures between graphene and Ir(111) are analyzed. The experimental results are compared to density functional theory calculations including dispersive forces. The existence of these phases under graphene and their absence on bare Ir(111) are discussed in terms of possible changes in the adsorbate-substrate interaction due to the presence of the graphene cover.