The integration of mixed ionic-electronic conducting separation membranes in catalytic membrane reactors can yield more environmentally safe and economically efficient processes. Concentration polarization effects are observed in these types of membranes when O2 permeating fluxes are significantly high. These undesired effects can be overcome by the development of new membrane reactors where mass transport and heat transfer are enhanced by adopting state-of-the-art microfabrication. In addition, careful control over the fluid dynamics regime by employing compact metallic reactors equipped with microchannels could allow the rapid extraction of the products, minimizing undesired secondary reactions. Moreover, a high membrane surface area to catalyst volume ratio can be achieved. In this work, a compact metallic reactor was developed for the integration of mixed ionic-electronic conducting ceramic membranes. An asymmetric all-La0.6Sr0.4Co0.2Fe0.8O3-δ membrane was sealed to the metallic reactor by the reactive air brazing technique. O2 permeation was evaluated as a proof of concept, and the influence of different parameters, such as temperature, sweep gas flow rates and oxygen partial pressure in the feed gas, were evaluated.

Asymmetric LSCF Membranes Utilizing Commercial Powders.

Powders of constant morphology and quality are indispensable for reproducible ceramic manufacturing. In this study, commercially available powders were characterized regarding their microstructural properties and screened for a reproducible membrane manufacturing process, which was done by sequential tape casting. Basing on this, the slurry composition and ratio of ingredients were systematically varied in order to obtain flat, crack-free green tapes suitable for upscaling of the manufacturing process. Debinding and sintering parameters were adjusted to obtain defect-free membranes with diminished bending. The crucial parameters are the heating ramp, sintering temperature, and dwell time. The microstructure of the asymmetric membranes was investigated, leading to a support porosity of approximately 35% and a membrane layer thickness of around 20 µm. Microstructure and oxygen flux are comparable to asymmetric La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) membranes manufactured from custom-made powder, showing an oxygen flux of > 1 mLcm-2min at 900 °C in air/Ar gradient.