ABSTRACT
Biomedical implants are important devices used for the repair or replacement of damaged or diseased tissues or organs. The success of implantation depends on various factors, such as mechanical properties, biocompatibility, and biodegradability of the materials used. Recently, magnesium (Mg)-based materials have emerged as a promising class of temporary implants due to their remarkable properties, such as strength, biocompatibility, biodegradability, and bioactivity. This review article aims to provide a comprehensive overview of current research works summarizing the above-mentioned properties of Mg-based materials for use as temporary implants. The key findings from in-vitro, in-vivo, and clinical trials are also discussed. Further, the potential applications of Mg-based implants and the applicable fabrication methods are also reviewed.
ABSTRACT
Magnesium samples reinforced with 0.7, 1.4, and 2.4 vol.% of Inconel 718 particles were prepared using a disintegrated melt deposition technique followed by hot extrusion. Mechanical properties, thermal expansion, and damping were studied with the aim of revealing the particle influence on the microstructure, texture, tensile and compressive behavior, thermal expansion coefficient, and internal friction. The flow stresses are significantly influenced by the test temperature and the vol.% of particles. A substantial asymmetry in the tensile and compressive properties was observed at lower temperatures. This asymmetry is caused by different deformation mechanisms operating in tension and compression. The fiber texture of extruded composite samples, refined grain sizes, and the increased dislocation density improved the mechanical properties. On the other hand, a decrease in the thermal expansion coefficient and internal friction was observed.
ABSTRACT
In this study, magnesium composites with nano-size boron nitride (BN) particulates of varying contents were synthesized using the powder metallurgy (PM) technique incorporating microwave-assisted two-directional sintering followed by hot extrusion. The effect of nano-BN addition on the microstructural and the mechanical behavior of the developed Mg/BN composites were studied in comparison with pure Mg using the structure-property correlation. Microstructural characterization revealed uniform distribution of nano-BN particulates and marginal grain refinement. The coefficient of thermal expansion (CTE) value of the magnesium matrix was improved with the addition of nano-sized BN particulates. The results of XRD studies indicate basal texture weakening with an increase in nano-BN addition. The composites showed improved mechanical properties measured under micro-indentation, tension and compression loading. While the tensile yield strength improvement was marginal, a significant increase in compressive yield strength was observed. This resulted in the reduction of tension-compression yield asymmetry and can be attributed to the weakening of the strong basal texture.