In this work, a surface cationized inorganic-organic hybrid foam was produced from porous geopolymer (GP) and cellulose nanocrystals (CNCs). GPs were synthesized from alkali-activated metakaolin using H2O2 as a blowing agent and hexadecyltrimethylammonium bromide (CTAB) as a surfactant. These highly porous GPs were combined at pH 7.5 with cationic CNCs that had been synthesized from dissolving pulp through periodate oxidation followed by cationization in a deep eutectic solvent. The GP-CNC hybrid foams were employed as reactive filters in the removal of the anionic dye, methyl orange (MO; 5-10 mg/L, pH 7). The effects of a mild acid wash and thermal treatments on the structure, properties, and adsorption capacity of the GPs with CNCs and MO were investigated. The CNCs aligned as films and filaments on the surfaces of the neutralized GPs and the addition of CNCs improved MO removal by up to 84% compared with the reference sample. In addition, CTAB was found to disrupt the attachment of CNCs on the pores and improve adsorption of MO in the GPs with and without CNCs.

Anionically Stabilized Cellulose Nanofibrils through Succinylation Pretreatment in Urea-Lithium Chloride Deep Eutectic Solvent.

Deep eutectic solvents (DESs) are green chemicals that have the potential to replace traditional solvents in chemical reactions. In this study, urea-LiCl DES was used successfully as a reaction medium in the anionic functionalization of wood cellulose with succinic anhydride. The effects of reaction temperature and time on the carboxyl content and yield were evaluated. The analyses of the degree of polymerization and crystallinity revealed that the DES was a nondegrading and nondissolving reaction medium. Three samples with the highest carboxyl contents were further nanofibrillated with a microfluidizer to diameters of 2-7 nm, as observed by atomic force microscopy. Samples treated at 70-80 °C for 2 h gave the best outcome and resulted in highly viscose and transparent gels. The sample treated at 90 °C contained larger nanoparticles and larger aggregates owing to the occurrence of possible side reactions but resulted in better thermal stability.