Fabrication of junction-free Cu nanowire networks via Ru-catalyzed electroless deposition and their application to transparent conducting electrodes.

Over the past few years, metal nanowire networks have attracted attention as an alternative to transparent conducting oxide materials such as indium tin oxide for transparent conducting electrode applications. Recently, electrodeposition of metal on nanoscale template is widely used for formation of metal network. In the present work, junctionless Cu nanowire networks were simply fabricated on a substrate by forming a nanostructured Ru with 80 nm width as a seed layer, followed by direct electroless deposition of Cu. By controlling the density of Ru nanowires or the electroless deposition time, we readily achieve desired transmittance and sheet resistance values ranging from ∼1 kΩ sq-1at 99% to 9 Ω sq-1at 89%. After being transferred to flexible substrates, the nanowire networks exhibited no obvious increase in resistance during 8000 cycles of a bending test to a radius of 2.5 mm. The durability was verified by evaluation of its heating performance. The maximum temperature was greater than 180 °C at 3 V and remained constant after three repeated cycles and for 10 min. Transmission electron microscopy and x-ray diffraction studies revealed that the adhesion between the electrolessly deposited Cu and the seed Ru nanowires strongly influenced the durability of the core-shell structured nanowire-based heaters.

Large-Area 2D-MXene Nanosheet Assemblies Using Langmuir-Schaefer Technique: Wrinkle formation.

The formation of uniform sheets of exfoliated MXene over a large area is important for improving their performance in practical applications. In this study, the Langmuir-Schaefer technique was employed to deposit uniform MXene sheets on a solid substrate and control the morphological structure over a large area. At the liquid-gas interface, MXene flakes were densely compressed into nanosheets with minimal gaps between them at 20 mN/m. Through further compression, the wrinkle morphologies of MXene sheets tend to be perpendicularly aligned to the compression direction. These wrinkle structures were also exhibited when MXene sheets were mixed in equal proportions with graphene oxide sheets. Owing to the close correlation of the morphologies of MXene films with the performance of MXene-based materials, the technique employed in this study can provide a route for applications requiring wrinkled MXene, ranging from nanoelectronic devices to energy storage materials, such as supercapacitors and battery electrodes.