ABSTRACT
In this study, novel silane acrylates, such as diethylene glycol diacrylate (DEGDA) and tetraethylene glycol diacrylate (TEGDA), containing ethylene glycol chains were synthesized and introduced into acrylic pressure-sensitive adhesives (PSAs) to regulate their peel strength and rheological properties. The synthesized silane acrylates effectively improved the cohesion and adhesive properties of the acrylic PSAs, even with only 1 wt% addition. In addition, the glass transition temperature and flexibility of acrylic PSAs were also affected by the increase in free volume induced by ethylene glycol chains. The silane acrylates also improved the viscoelasticity of the acrylic PSAs, which exhibited excellent recovery (62-96%) and stress relaxation (>90%) properties owing to the increased elasticity. Additionally, the acrylic PSAs prepared with the silane acrylates showed excellent optical properties (transmittance ≥ 90%, haze ≤ 1%) and exhibited behavior suitable for application in flexible displays from a comprehensive perspective.
ABSTRACT
EPOSS of polyhedral oligomeric silsesquioxanes (POSS) mixture structure and LPSQ of ladder-like polysilsesquioxane (LPSQ) structure were synthesized via sol-gel reaction. EPSQ had a high molecular weight due to polycondensation by potassium carbonate. The EPSQ film showed uniform surface morphology due to regular double-stranded structure. In contrast, the EPOSS-coated film showed nonuniform surface morphology due to strong aggregation. Due to the aggregation, the EPOSS film had shorter d-spacing (d1) than the EPSQ film in XRD analysis. In pencil hardness and nanoindentation analysis, EPSQ film showed higher hardness than the EPOSS film due to regular double-stranded structure. In addition, in the in-folding (r = 0.5 mm) and out-folding (r = 5 mm) tests, the EPSQ film did not crack unlike the EPOSS coated film.
ABSTRACT
Hydrophilic acrylic pressure-sensitive adhesives (PSAs) were synthesized by controlling the contents of 2-ethylhexyl acrylate (EHA), isobornyl acrylate (IBOA), and 2-hydroxyethyl acrylate (HEA); especially, the characteristic change of the HEA content was analyzed. Surface contact angle of acrylic PSA film decreased from 77.87° to 70.23° in the case of Acryl-2 to Acryl-8 (below HEA 10 wt %). However, the surface contact angle of Acryl-10 to Acryl-40 (HEA 10 wt % to 40 wt %) increased up to 92.29°, indicating hydrophobicity. All acrylic PSA films showed high adhesive force above 1800 gf/25 mm. According to X-ray diffraction (XRD) measurement, hydrophilic acrylic PSAs exhibited amorphous property and it was confirmed that the morphology of acrylic PSA film was significantly affected by the flexibility of the polymer chain and the strength of hydrogen bonding. The affinity with hydrophilic materials for acrylic PSA films was evaluated by T-type peel test, confirming that the affinity with hydrophilic materials is determined by the hydrophilicity of the acrylic PSA film. The synthesized acrylic PSA film is non-toxic regardless of the hydrophilicity.