Preparation of NiAl-AlMg6 Functionally Graded Composite Using the Energy of a Highly Exothermic Ti-C Mixture during Self-Propagating High-Temperature Synthesis.

A functionally graded composite NiAl-AlMg6 was prepared using the pressure of gaseous reaction products (impurity gases) produced during the synthesis of reactive powders in a sealed reactor. It has been shown that this method can be used to prepare a NiAl/AlMg6 composite with both chaotically oriented pores in the NiAl layer and unidirectionally oriented pores (lotus-type pores). The pore shape in NiAl was found to be dependent on the pressure of the impurity gases and hydrogen present in the starting titanium powder. A mechanism for pore formation in NiAl and AlMg6 composite during SHS is proposed. Thus, functionally graded high-temperature composites can be produced by SHS in a sealed reactor using the chemical reaction energy and the pressure of impurity gases and hydrogen. Additionally, minimizing the influence of impurity gases on the contact zone increases the interface area between NiAl and AlMg6.

Synthesis of NiAl Intermetallic Compound under Shock-Wave Extrusion.

This paper presents the implementation of the first stage of a study on the synthesis of the intermetallic compound in the Ni-Al system under shock-wave extrusion (SWE). A method was developed and experiments involving SWE of the reactive Ni-Al powder mixture were carried out. As a result, it was possible to obtain up to 56 vol.% of the final product and achieve 100% synthesis of NiAl. The results of metallographic analysis indicate that the process of high-velocity collapse of the tube created conditions for the formation of a cumulative flow, which directly affects the phase formation in NiAl. It was shown that the presence of the central hole in the powder sample reduced the effect of the Mach stem on the homogeneity of the NiAl structure. It was also determined that with a central hole with a 5 mm diameter, the effect of the Mach stem could not be observed at all. The goals of further studies are achieving 90-100 vol.% of the final product and reducing the porosity in the final product. Preliminary experimental studies have shown great potential for SWE to produce composite metal-intermetallic materials.