Developing a Simple, Effective, and Quick Process to Make Silver Nanowires with a High Aspect Ratio.

A growing number of people are interested in using silver nanowires (AgNWs) as potential transparent and conductive materials. The production of high-performance and high-throughput AgNWs was successfully optimized in this work using a one-step, straightforward, and reproducible modified polyol approach. The factors influencing the morphology of the silver nanowires have undergone extensive research in order to determine the best-optimized approach for producing AgNWs. The best AgNW morphology, with a length of more than 50 m and a diameter of less than 35 nm (aspect ratio is higher than 1700), was discovered to be produced by a mixture of 44 mM AgNO3, 134 mM polyvinylpyrrolidone (PVP) (Mo.Wt 40,000), and 2.4 mM KCl at 160 °C with a stirring rate of 100 rpm. With our improved approach, the overall reaction time was cut from almost an hour with the conventional polyol method to a few minutes. Scanning electron microscopy (SEM), X-ray diffraction (XRD), and ultraviolet (UV) spectroscopy were used to characterize AgNWs. The resultant AgNWs' dispersion was cleaned using a centrifuge multiple times before being deposited on glass and PET substrates at room temperature. In comparison to commercial, delicate, and pricey indium-doped tin oxide (ITO) substrates, the coated samples displayed exceptionally good sheet resistance of 17.05/sq and optical haze lower than 2.5%. Conclusions: Using a simple one-step modified polyol approach, we were able to produce reproducible thin sheets of AgNWs that made excellent, flexible transparent electrodes.

Novel Magnetic Zinc Oxide Nanotubes for Phenol Adsorption: Mechanism Modeling.

Considering the great impact of a material's surface area on adsorption processes, hollow nanotube magnetic zinc oxide with a favorable surface area of 78.39 m²/g was fabricated with the assistance of microwave technology in the presence of poly vinyl alcohol (PVA) as a stabilizing agent followed by sonic precipitation of magnetite nano-particles. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) micrographs identified the nanotubes' morphology in the synthesized material with an average aspect ratio of 3. X-ray diffraction (XRD) analysis verified the combination of magnetite material with the hexagonal wurtzite structure of ZnO in the prepared material. The immobilization of magnetite nanoparticles on to ZnO was confirmed using vibrating sample magnetometry (VSM). The sorption affinity of the synthesized magnetic ZnO nanotube for phenolic compounds from aqueous solutions was examined as a function of various processing factors. The degree of acidity of the phenolic solution has great influence on the phenol sorption process on to magnetic ZnO. The calculated value of ΔH° designated the endothermic nature of the phenol uptake process on to the magnetic ZnO nanotubes. Mathematical modeling indicated a combination of physical and chemical adsorption mechanisms of phenolic compounds on to the fabricated magnetic ZnO nanotubes. The kinetic process correlated better with the second-order rate model compared to the first-order rate model. This result indicates the predominance of the chemical adsorption process of phenol on to magnetic ZnO nanotubes.