Two-Photon Excitation Spectroscopy of Silicon Quantum Dots and Ramifications for Bio-Imaging.

Two-photon excitation in the near-infrared (NIR) of colloidal nanocrystalline silicon quantum dots (nc-SiQDs) with photoluminescence also in the NIR has potential opportunities in the field of deep biological imaging. Spectra of the degenerate two-photon absorption (2PA) cross section of colloidal nc-SiQDs are measured using two-photon excitation over a spectral range 1.46 < ℏω < 1.91 eV (wavelength 850 > λ > 650 nm) above the two-photon band gap Eg(QD)/2, and at a representative photon energy ℏω = 0.99 eV (λ = 1250 nm) below this gap. Two-photon excited photoluminescence (2PE-PL) spectra of nc-SiQDs with diameters d = 1.8 ± 0.2 nm and d = 2.3 ± 0.3 nm, each passivated with 1-dodecene and dispersed in toluene, are calibrated in strength against 2PE-PL from a known concentration of Rhodamine B dye in methanol. The 2PA cross section is observed to be smaller for the smaller diameter nanocrystals, and the onset of 2PA is observed to be blue shifted from the two-photon indirect band gap of bulk Si, as expected for quantum confinement of excitons. The efficiencies of nc-SiQDs for bioimaging using 2PE-PL are simulated in various biological tissues and compared to efficiencies of other quantum dots and molecular fluorophores and found to be comparable or superior at greater depths.

Silicon Nanocrystal Superlattice Nucleation and Growth.

Colloidal dodecene-passivated silicon (Si) nanocrystals were dispersed in hexane or chloroform and deposited onto substrates as face-centered cubic superlattices by slowly evaporating the solvent. The uniformity of the nanocrystals enables extended order; however, the solvent and the evaporation protocol significantly influence the self-assembly process, determining the morphology of the films, the extent of order, and the superlattice orientation on the substrate. Chloroform yielded superlattices with step-flow growth morphologies and (111)SL, (100)SL, and (110)SL orientations. Hexane led to mostly island morphologies when evaporated at room temperature with exclusively (111)SL orientations. Higher evaporation temperatures led to more extensive step-flow deposition. A model for the surface diffusion of nanocrystals adsorbed on the superlattice surface is developed.