ABSTRACT
The growing popularity of poly(lactic acid) (PLA) can be attributed to its favorable attributes, such as excellent compostability and robust mechanical properties. Two notable limitations of PLA are its high brittleness and slow biodegradation rate. Both of blending and copolymerization strategies work well to improve PLA's toughness while sacrificing the good tensile strength and modulus properties of PLA. One of the most effective and economical approaches to address this challenge is to incorporate natural reinforcing agents into the toughened PLA system, thereby simultaneously promoting the biodegradation rate of PLA. Nevertheless, the enhancement of tensile strength and modulus is accompanied by a notable decrease in elongation. Therefore, this review provides comprehensive information on the literature works related to the tensile strength, modulus, elongation at break and impact strength of the toughened PLA and its natural fiber reinforced composites. The impact of natural reinforcing agent on the tensile fracture mechanism as well as the synergistic effect on strengthening and toughening performance will be discussed. This review also focuses on the factors boosting the biodegradability of toughened PLA blend by using natural reinforcing fiber. Review presents potential future insights into the development of biodegradable and balanced strengthened-toughened PLA based advanced materials.
ABSTRACT
Over the last few decades, processing and compatibility have become challenging and interesting investigation areas of polymer matrix nanocomposites. This study investigated the addition of maleic anhydride (MAH) at different ratios with graphene nanoplatelets (GnPs) in poly(lactic acid)/modified natural rubber/polyaniline/GnP (PLA/m-NR/PANI/GnP) nanocomposites via two processing methods: a two-step technique and a one-pot technique. The former technique involved first preparing a master batch of PLA grafted with MAH, followed by a second step involving the melt blending of the nanocomposite (T1) using MAH-g-PLA. On the other hand, the one-pot technique involved the direct mixing of MAH during the melt-blending process (T2). The mechanical, morphological and thermal properties of the prepared nanocomposites were investigated. The findings showed that adding MAH significantly improved the tensile strength and elongation at break by about 25% for PLA/m-NR/PANi/GnP nanocomposites, with an optimal ratio of 1:1 of MAH-g-PLA to GnP loading using the T1 technique. FTIR analysis confirmed the chemical interaction between MAH and PLA for T1 nanocomposites, which exhibited improved phase morphology with smoother surfaces. MAH-compatibilized nanocomposites had enhanced thermal stabilities when compared to the sample without a compatibilizer. The findings show that the compatibilized PLA nanocomposite is potentially suitable for bio-inspired materials.
ABSTRACT
Thermoplastic natural rubber (TPNR) was compounded with graphene nanoplatelets (GNP) via ultrasonication and melt blending. The effects of ultrasonication period (1-4 hours) and GNP weight fraction (0.5, 1.0, 1.5 and 2.0 wt.%) on the mechanical, thermal and conductivity properties were investigated. Results showed that the 3 hours of ultrasonic treatment on LNR/GNP gave the greatest improvement in tensile strength of 25.8% (TPNR/GNP nanocomposites) as compared to those without ultrasonication. The TPNR nanocomposites containing 1.5 wt.% GNP exhibited the highest strength (16 MPa for tensile, 14 MPa for flexural and 11 kJm-2 for impact) and modulus (556 MPa and 869 MPa for tensile and flexural, respectively). The incorporation of GNP had enhanced the thermal stability. It can be concluded that the GNP had imparted the thermally and electrically conductive nature to the TPNR blend.