ABSTRACT
Electron beam additive wire-feed manufacturing of Cu-3wt.%S-0.8wt.%Mn bronze thin wall on a stainless steel substrate has been carried out at heat input levels of 0.19, 0.25, and 0.31 kJ/mm. The microstructures of as-deposited metal ranged from low aspect ratio columnar with equiaxed grain layers to zig-zagged and high aspect ratio columnar, as depended on the heat input. Post-deposition annealing at 900 °C for 6 h resulted in recrystallization of the high aspect ratio columnar grains with further grain growth by boundary migration. Pre-deformation by 10% thickness reduction and then annealing at 900 °C for 6 h also allowed obtaining recrystallized grain structures with less fraction of twin boundaries but higher fraction of high-angle ones, as compared to those of only annealed sample. Pre-deformation and ensuing annealing allowed simultaneous increasing of the ultimate tensile strength and strain-to-fracture.
ABSTRACT
In this work, the method of electron beam additive manufacturing (EBAM) was used to fabricate a Cu-based alloy possessing a shape memory effect. Electron beam additive technology is especially relevant for copper and its alloys since the process is carried out in a vacuum, which makes it possible to circumvent oxidation. The main purpose of the study was to establish the influence of the printing parameters on the structure of the obtained products, their phase composition, mechanical properties, dry friction behavior, and the structure-phase gradient that formed in Cu-Al-Mn alloy samples during electron beam layer-by-layer printing. The results of the study allowed us to reveal that the structure-phase composition, the mechanical properties, and the tribological performance of the fabricated material are mainly affected by the magnitude of heat input during electron beam additive printing of Cu-Al-Mn alloy. High heat input values led to the formation of the ß1' + α decomposed structure. Low heat input values enabled the suppression of decomposition and the formation of an ordered 1 structure. The microhardness values were distributed on a gradient from 2.0 to 2.75 GPa. Fabricated samples demonstrated different behaviors in friction and wear depending on their composition and structure, with the value of the friction coefficient lying in the range between 0.1 and 0.175.
ABSTRACT
A gradient transition zone was obtained using electron beam deposition from AA4047 wire on AA7075 substrate and characterized for microstructures, tensile strength and corrosion resistance. The microstructure of the transition zone was composed of aluminum alloy grains, Al/Si eutectics and Fe-rich and Si-rich particles. Such a microstructure provided strength comparable to that of AA7075-T42 substrate but more intense corrosion due to the higher amount of anodic Mg2Si particles. The as-deposited AA4047 zone formed above the transition zone was composed of aluminum alloy dendrites and interdendritic Al/Si eutectics with low mechanical strength and high corrosion potential.
ABSTRACT
Electron beam additive wire-feed deposition of Cu-7.5wt.%Al bronze on a stainless-steel substrate has been carried out at heat input levels 0.21, 0.255, and 0.3 kJ/mm. The microstructures formed at 0.21 kJ/mm were characterized by the presence of both zigzagged columnar and small equiaxed grains with 10% of Σ3 annealing twin grain boundaries. No equiaxed grains were found in samples obtained at 0.255 and 0.3 kJ/mm. The zigzagged columnar ones were only retained in samples obtained at 0.255 kJ/mm. The fraction of Σ3 boundaries reduced at higher heat input values to 7 and 4%, respectively. The maximum tensile strength was achieved on samples obtained with 0.21 kJ/mm as tested with a tensile axis perpendicular to the deposited wall's height. More than 100% elongation-to-fracture was achieved when testing the samples obtained at 0.3 kJ/mm (as tested with a tensile axis coinciding with the wall's height).