ABSTRACT
Nanostructured niobium-titanium carbonitrides, (Nb,Ti)C1-xNx, with the cubic-rock salt structure are prepared without the use of reactive gases via thermal treatment (700-1200 °C) under nitrogen of mixtures of guanidine carbonate and ammonium niobate (V) oxalate hydrate, with addition of ammonium titanyl oxalate monohydrate as a titanium source. The bulk structure and chemical composition of the materials are characterized using powder X-ray diffraction (XRD) and powder neutron diffraction, elemental homogeneity is studied using energy dispersive spectroscopy (EDS) mapping using transmission electron microscopy (TEM), and surface chemical analysis is examined using X-ray photoelectron spectroscopy (XPS). Nanoscale crystallites of between 10 and 50 nm are observed by TEM, where EDS reveals the homogeneity of metal distribution for the mixed-metal materials. Titanium carbonitrides are found to be air sensitive, reacting with air under ambient conditions, while titanium-niobium carbonitrides are found to degrade in aqueous sulfuric acid. The niobium carbonitrides, however, show some stability toward acidic solutions. Materials are produced with composition NbC1-xNx with x between 0.35 and 0.45, and more carbon-rich materials (x ≈ 0.35) are found as the synthesis temperature is increased, as proven by Rietveld refinement of crystal structure against powder neutron diffraction data. Despite phase purity seen by diffraction and negligible bulk carbon content, XPS shows a complex surface chemistry for the NbC1-xNx materials, with evidence for Nb2O5-like oxide species in a carbon-rich environment. The NbC1-xNx prepared at 900 °C has a surface area around 50 m2 g-1, making it suitable as a catalyst support. Loading with iridium provides a material active for the oxygen evolution reaction in 0.1 M sulfuric acid, with minimal leaching of either Nb or Ir after 1000 cycles.
ABSTRACT
Pyrochlore iridates (Na,Ca)2-xIr2O6·H2O are acid-stable electrocatalysts that are candidates for use in electrolysers and fuel cells. Ir LIII-edge X-ray absorption fine structure spectroscopy in 1 M H2SO4 at oxygen evolution conditions suggests the involvement of the electrons from the conduction band of the metallic particles, rather than just surface iridium reacting.
ABSTRACT
A synthesis method for the preparation of mixed manganese-ruthenium oxides is presented along with a detailed characterisation of the solids produced. The use of 1 M aqueous sulfuric acid mediates the redox reaction between KRuO4, KMnO4 and Mn2+ to form ternary oxides. At reaction temperature of 100 °C the products are mixtures of α-MnO2 (hollandite-type) and ß-MnO2 (rutile-type), with some evidence of Ru incorporation in each from their expanded unit cell volumes. At reaction temperature of 200 °C solid-solutions ß-Mn1-xRuxO2 are formed and materials with x ≤ 0.6 have been studied. The amount of Ru included in the oxide is greater than expected from the ratio of metals used in the synthesis, as determined by elemental analysis, implying that some Mn remains unreacted in solution. Powder X-ray diffraction (XRD) shows that while the unit cell volume expands in a linear manner, following Vegard's law, the tetragonal lattice parameters, and the a/c ratio, do not follow the extrapolated trends: this anisotropic behaviour is consistent with the different local coordination of the metals in the end members. Powder XRD patterns show increased peak broadening with increasing ruthenium content, which is corroborated by electron microscopy that shows nanocrystalline material. X-ray absorption near-edge spectra show that the average oxidation state of Mn in the solid solutions is reduced below +4 while that of Ru is increased above +4, suggesting some redistribution of charge. Analysis of the extended X-ray absorption fine structure provides complementary local structural information, confirming the formation of a solid solution, while X-ray photoelectron spectroscopy shows that the surface oxidation states of both Ru and Mn are on average lower than +4, suggesting a disordered surface layer may be present in the materials.
ABSTRACT
The pyrochlore solid solution (Na(0.33)Ce(0.67))2(Ir(1-x)Ru(x))2O7 (0≤x≤1), containing B-site Ru(IV) and Ir(IV) is prepared by hydrothermal synthesis and used as a catalyst layer for electrochemical oxygen evolution from water at pH<7. The materials have atomically mixed Ru and Ir and their nanocrystalline form allows effective fabrication of electrode coatings with improved charge densities over a typical (Ru,Ir)O2 catalyst. An inâ situ study of the catalyst layers using XANES spectroscopy at the Ir L(III) and Ru Kâ edges shows that both Ru and Ir participate in redox chemistry at oxygen evolution conditions and that Ru is more active than Ir, being oxidized by almost one oxidation state at maximum applied potential, with no evidence for ruthenate or iridate in +6 or higher oxidation states.