Sterically Controlled Synthesis of Amine-Free CsPbBr3 Nanoplatelets for Stable, Pure-Blue Light Emission.

Metal halide perovskite nanoplatelets (NPLs) have demonstrated excellent optical properties for light-emitting applications and achieved tunable blue luminescence through thickness control. However, their translation into electronic devices has lagged behind due to poor colloidal and film stability. The main reason for this is the deprotonation of their surface-capped ammonium passivating ligands, resulting in NPL aggregation. Here we report the first facile synthesis of amine-free pure-blue CsPbBr3 NPLs with outstanding thermal and light stability. This is achieved by utilizing an amine-free phosphine oxide route with a surface capping molecule exhibiting large steric hindrance to prevent NPL aggregation. Two-dimensional nuclear magnetic resonance (2D NMR) spectroscopy suggests slower ligand exchange in amine-free NPLs compared to the conventional NPLs, which can be attributed to the strong binding strength of the designated ligand. Consequently, the amine-free NPLs exhibited superior stability against radiation, heat and moisture. We further demonstrate the importance of acid-base equilibrium in this amine-free synthesis route. Through solvent neutralization and passivation with various alkali carbonates, the resulting NPLs attained near-unity photoluminescence quantum yield (PLQY) and pure blue emission.

Enhanced CO2 Reactive Capture and Conversion Using Aminothiolate Ligand-Metal Interface.

Metallic catalyst modification by organic ligands is an emerging catalyst design in enhancing the activity and selectivity of electrocatalytic carbon dioxide (CO2) reactive capture and reduction to value-added fuels. However, a lack of fundamental science on how these ligand-metal interfaces interact with CO2 and key intermediates under working conditions has resulted in a trial-and-error approach for experimental designs. With the aid of density functional theory calculations, we provided a comprehensive mechanism study of CO2 reduction to multicarbon products over aminothiolate-coated copper (Cu) catalysts. Our results indicate that the CO2 reduction performance was closely related to the alkyl chain length, ligand coverage, ligand configuration, and Cu facet. The aminothiolate ligand-Cu interface significantly promoted initial CO2 activation and lowered the activation barrier of carbon-carbon coupling through the organic (nitrogen (N)) and inorganic (Cu) interfacial active sites. Experimentally, the selectivity and partial current density of the multicarbon products over aminothiolate-coated Cu increased by 1.5-fold and 2-fold, respectively, as compared to the pristine Cu at -1.16 VRHE, consistent with our theoretical findings. This work highlights the promising strategy of designing the ligand-metal interface for CO2 reactive capture and conversion to multicarbon products.