RSC Adv ; 11(45): 28072-28080, 2021 Aug 16.
Article in English | MEDLINE | ID: mdl-35480771

ABSTRACT

Most studies to date on SnSe thermal transport are focused on single crystals and polycrystalline pellets that are obtained using high-temperature processing conditions and sophisticated instruments. The effects of using sub-10 nm-size SnSe nanocrystals on the thermal transport and thermoelectric properties have not been studied to the best of our knowledge. Here, we report the synthesis of sub-10 nm colloidal surfactant-free SnSe NCs at a relatively low temperature (80 °C) and investigate their thermoelectric properties. Pristine SnSe NCs exhibit p-type transport but have a modest power factor of 12.5 µW m-1 K-2 and ultralow thermal conductivity of 0.1 W m-1 K-1 at 473 K. Interestingly, the one-step post-synthesis treatment of NC film with methylammonium iodide can switch the p-type transport of the pristine film to n-type. The power factor improved significantly to 20.3 µW m-1 K-2, and the n-type NCs show record ultralow thermal conductivity of 0.14 W m-1 K-1 at 473 K. These surfactant-free SnSe NCs were then used to fabricate flexible devices that show superior performance to rigid devices. After 20 bending cycles, the flexible device shows a 34% loss in the power factor at room temperature (295 K). Overall, this work demonstrates p- and n-type transport in SnSe NCs via the use of simple one-step post-synthesis treatment, while retaining ultralow thermal conductivity.

2.
J Phys Chem A ; 124(23): 4855-4860, 2020 Jun 11.
Article in English | MEDLINE | ID: mdl-32396362

ABSTRACT

Single-particle spectroscopy has demonstrated great potential for analyzing the microscopic behavior of various nanoparticles (NPs). However, high-resolution optical imaging of these materials at the nanoscale is still very challenging. Here, we present an experimental setup that combines high sensitivity of time-correlated single-photon counting (TCSPC) techniques with atomic force microscopy (AFM). This system enables single-photon detection with a time resolution of 120 ps and a spatial resolution of 5 nm. We utilize the setup to investigate the photoluminescence (PL) characteristics of both zero-dimensional (0D) and three-dimensional (3D) perovskite nanocrystals and establish a correlation between the particles' sizes, their PL blinking, and the lifetime behavior. Our system demonstrates an unprecedented level of information, opening the door to understanding the morphology-luminescence correlation of various nanosystems.