ABSTRACT
The reduction of pellets composed of individual CeO2, Nd2O3 and a La2O3-Nd2O3-CeO2 mixture by lithium extracted on a cathode during lithium chloride electrolysis at 650 °C was studied. The methods of cyclic voltammetry, electron microscopy, including determination of the elemental composition of the studied objects, and X-ray diffraction analysis were applied for the present study. The reduction degree of rare-earth metal (REM) oxides was determined using both the bromine method and reduction melting of the samples in the graphite crucible. The formation of the metallic phase composed of the rare-earth elements (REEs) was not observed even at the cathode potentials, corresponding to the formation of the liquid alkali metal phase, and lithium extraction, which, in the quantitative ratio, exceeds greatly the values needed for the reduction reaction. CeO2 was found to reduce to Ce2O3.
ABSTRACT
The NdF3 solubility in molten eutectic FLiNaK, which is a conceivable medium for a molten salt reactor (MSR), was determined by the quasi-binary phase diagram FLiNaK-NdF3. The eutectic mixture FLiNaK was prepared by direct melting of components LiF, NaF and KF·HF. The acidic anhydrous salt (KF·HF) was used instead of the hygroscopic KF. The NdF3 was sintered by hydrofluorination of Nd2O3. The oxygen impurity in the prepared eutectic FLiNaK, determined by an oxygen analyzer LECO OH836, was 0.036 wt.%, whereas the NdF3 contained 0.04 wt.% of oxygen. A part of the FLiNaK-NdF3 quasi-binary phase diagram was obtained using two thermal analysis techniques: differential thermal analysis (DTA) and differential scanning calorimetry (DSC). The FLiNaK-NdF3 phase diagram in the region of 0-30 mol.% NdF3 contains one eutectic at 2 mol.% NdF3 and 450 °C and two peritectic points: 8 mol.% NdF3 at 500 °C and 22 mol.% NdF3 at 575 °C. The region of the FLiNaK-NdF3 phase diagram below the liquidus line is rather complicated due to the complex structure of the multicomponent system in its molten state, as in its solid state. The NdF3 solubility in FLiNaK is about 5 mol.% at 490 °C and 29 mol.% at 700 °C; this means that the process of the MA transmutation in the MSR can be carried out in molten FLiNaK with a content of actinides as high as 15-20 mol.% in the temperature range of 550-650 °C.