ABSTRACT
The phase transition from the non-polar alpha-phase to the polar beta-phase of poly(vinylidene fluoride) (PVDF) has been investigated using micro-Raman spectroscopy, which is advantageous because it is a nondestructive technique. Films of alpha-PVDF were subjected to stretching under controlled rates at 80 degrees C, while the transition to beta-PVDF was monitored by the decrease in the Raman band at 794 cm(-1) characteristic of the alpha-phase, along with the concomitant increase in the 839 cm(-1) band characteristic of the beta-phase. The alpha-->beta transition in our PVDF samples could be achieved even for the sample stretched to twice (2x-stretched) the initial length and it did not depend on the stretching rate in the range between 2.0 and 7.0 mm/min. These conclusions were corroborated by differential scanning calorimetry (DSC) and X-ray diffraction experiments for PVDF samples processed under the same conditions as in the Raman scattering measurements. Poling with negative corona discharge was found to affect the alpha-PVDF morphology, improving the Raman bands related to this crystalline phase. This effect is minimized for films stretched to higher ratios. Significantly, corona-induced effects could not be observed with the other experimental techniques, i.e., X-ray diffraction and infrared spectroscopy.
Subject(s)
Crystallography/methods , Materials Testing/methods , Polyvinyls/analysis , Polyvinyls/chemistry , Spectrum Analysis, Raman/methods , Membranes, Artificial , Phase Transition , Physical Stimulation/methods , Stress, Mechanical , Temperature , Tensile StrengthABSTRACT
BACKGROUND: The aim of this study was to evaluate the action of tamoxifen on the endometrium in states of chronic anovulation. METHODS: Thirty-eight rats inducted to persistent estrous (testosterone propionate) confirmed by hormonal colpocytology were divided into a control and an experimental group; the latter received tamoxifen and had fragments of the uterine horns processed for morphological and morphometrical analysis. Data were analysed statistically by the Mann-Whitney and Student's t tests. RESULTS: Our findings revealed minor uterine weight, epithelial thickness; number of endometrial glands and low eosinophil counts in the group that received tamoxifen. These results were statistically significant. We often observed areas of metaplasic stratified squamous epithelium between cylindrical epithelial cells in both groups. CONCLUSIONS: Our results indicate that antiestrogenic effect of tamoxifen was only partial in persistent estrous, since there was no blocking against the squamous metaplasia of the endometrium.