1.
ACS Omega ; 8(40): 36966-36977, 2023 Oct 10.
Article in English | MEDLINE | ID: mdl-37841155

ABSTRACT

Photodetection plays an essential role in the visible-light zone and is important in modern science and technology owing to its potential applications in various fields. Fabrication of a stable photodetector remains a challenge for researchers. We demonstrated a high-response/recovery and self-powered undoped ZnO (UZO) and Cu-doped ZnO (CZO) thin film-based visible-light photodetector fabricated on a cost-effective Si substrate using reactive cosputtering. The structural, morphological, and optical properties of CZO and UZO thin films have been examined using X-ray diffraction, field emission scanning electron microscopy, X-ray photoelectron spectroscopy, atomic force microscopy, and photoluminescence spectroscopy. The results of the CZO/n-Si photodetector compared with those of the undoped ZnO (UZO)/n-Si photodetector show that the CZO/n-Si exhibits a higher on/off ratio, responsivity, and detectivity than UZO/n-Si. Also, the CZO/n-Si photodetector shows high stability and reproducibility over 20 cycles after 180 days. A relative study of CZO/n-Si- and UZO/n-Si-based photodetectors reveals the enhanced performance of the CZO/n-Si photodetector, which has a high on/off ratio of ∼300 with a high specific detectivity of 2.8 × 1010 Jones for 75 mW visible light. The prepared self-powered CZO/n-Si/Ag thin film-based visible-light photodetector paves the way for the development of high-performance photodetector designs.

2.
Sci Rep ; 13(1): 14039, 2023 08 28.
Article in English | MEDLINE | ID: mdl-37640751

ABSTRACT

Microbial pathogens are known for causing great environmental stress, owing to which emerging challenges like lack of eco-friendly remediation measures, development of drug-resistant and mutational microbial strains, etc., warrants novel and green routes as a stepping stone to serve such concerns sustainably. In the present study, palladium (Pd) doped manganese (II, III) oxide (Mn3O4) nanoparticles (NPs) were synthesized using an aqueous Syzygium aromaticum bud (ASAB) extract. Preliminary phytochemical analysis of ASAB extract indicates the presence of polyphenolics such as phenols, alkaloids, and flavonoids that can act as potential capping agents in NPs synthesis, which was later confirmed in FTIR analysis of pure and Pd-doped Mn3O4 NPs. XRD, Raman, and XPS analyses confirmed the Pd doping in Mn3O4 NPs. FESEM and HRTEM study reveals the mixed morphologies dominated by nanocorns appearance. Zeta potential investigation reveals high stability of the synthesized NPs in colloidal solutions. The developed Pd-doped Mn3O4 NPs were tested against two fungal phytopathogens, i.e., Sclerotinia sclerotiorum and Colletotrichum gloeosporioides, known for causing great economic losses in yield and quality of different plant species. The antifungal activity of synthesized Pd-doped Mn3O4 NPs displayed a dose-dependent response with a maximum of ~92%, and ~72% inhibition was recorded against S. sclerotiorum and C. gloeosporioides, respectively, at 1000 ppm concentration. However, C. gloeosporioides demonstrated higher sensitivity to Pd-doped Mn3O4 NPs upto 500 ppm) treatment than S. sclerotiorum. The prepared NPs also showed significant antibacterial activity against Enterococcus faecalis. The Pd-doped Mn3O4 NPs were effective even at low treatment doses, i.e., 50-100 ppm, with the highest Zone of inhibition obtained at 1000 ppm concentration. Our findings provide a novel, eco-benign, and cost-effective approach for formulating a nanomaterial composition offering multifaceted utilities as an effective antimicrobial agent.


Subject(s)
Anti-Infective Agents , Manganese , Animals , Palladium/pharmacology
3.
ACS Omega ; 8(32): 29663-29673, 2023 Aug 15.
Article in English | MEDLINE | ID: mdl-37599967

ABSTRACT

In view of facile, cost-effective, and environmentally friendly synthetic methods, palladium-doped copper oxide (Pd-CuO) nanoparticles have been synthesized from Ocimum sanctum (commonly known as "Tulsi") phytoextract for gas-sensing applications. The structural, morphological, and compositional properties of Pd-doped CuO nanoparticles were studied using various techniques such as XRD, FESEM, XPS, and EDX. The characterization results confirmed the doping of Pd on CuO nanoparticles, and Pd-CuO nanostructures appear as nanoflakes in FESEM analysis. The gas-sensing response of Pd (1.12 wt %)-CuO nanoflake-based sensor was measured at 5-100 ppm concentration of different gases, NO2, H2S, NH3, and H2, at 125 °C. Gas-sensing tests reveal that the sensitivity of the sensor were 81.7 and 38.9% for 100 and 5 ppm concentrations of NO2, respectively, which was significantly greater than that of pure CuO. The response and recovery times of the sensor were 72 and 98 s for 100 ppm of NO2 gas, while they were 90 and 50 s for 5 ppm NO2. The calculated limit of detection (LOD) value of the sensor is 0.8235. This appealing LOD is suitable for real-time gas detection. The gas sensor was found to exhibit excellent selectivity toward NO2 gas and repeatability and stability in humid (80%) conditions. The Pd doping in CuO nanostructures plays a significant role in escalating the sensitivity and selectivity of CuO-based NO2 gas sensor suitable to work at low operating temperatures.

4.
Nanoscale Adv ; 5(3): 805-819, 2023 Jan 31.
Article in English | MEDLINE | ID: mdl-36756497

ABSTRACT

The different dyes used and discharged in industrial settings and microbial pathogenic issues have raised serious concerns about the content of bodies of water and the impact that dyes and microbes have on the environment and human health. Efficient treatment of contaminated water is thus a major challenge that is of great interest to researchers around the world. In the present work, we have fabricated functionalized silver-doped ZnO nanoparticles (Ag-doped ZnO NPs) via a hydrothermal method for wastewater treatment. X-ray photoelectron spectroscopy analysis confirmed the doping of Ag with ZnO NPs, and X-ray diffractometry analysis showed a decreasing trend in the crystallite size of the synthesized ZnO NPs with increased Ag concentration. Field emission scanning electron microscopy study of pure ZnO NPs and Ag-doped ZnO NPs revealed nanocrystal aggregates with mixed morphologies, such as hexagonal and rod-shaped structures. Distribution of Ag on the ZnO lattice is confirmed by high-resolution transmission electron microscopy analysis. ZnO NPs with 4 wt% Ag doping showed a maximum degradation of ∼95% in 1.5 h of malachite green dye (80 mg L-1) under visible light and ∼85% in 4 h under dark conditions. Up to five successive treatment cycles using the 4 wt% Ag-doped ZnO NP nanocatalyst confirmed its reusability, as it was still capable of degrading ∼86% and 82% of the dye under visible light and dark conditions, respectively. This limits the risk of nanotoxicity and aids the cost-effectiveness of the overall treatment process. The synthesized NPs showed antibacterial activity in a dose-dependent manner. The zone of inhibition of the Ag-doped ZnO NPs was higher than that of the pure ZnO NPs for all doping content. The studied Ag-doped ZnO NPs thus offer a significant eco-friendly route for the effective treatment of water contaminated with synthetic dyes and fecal bacterial load.

5.
Nanomaterials (Basel) ; 9(10)2019 Oct 11.
Article in English | MEDLINE | ID: mdl-31614501

ABSTRACT

Biogenic silica (b-SiO2) nanopowders from rice husk ash (RHA) were prepared by chemical method and their bacterial compatibility/toxicity was analyzed. The X-ray diffractometry (XRD) patterns of the b-SiO2 nanopowders indicated an amorphous feature due to the absence of any sharp peaks. Micrographs of the b-SiO2 revealed that sticky RHA synthesized SiO2 nanopowder (S1) had clustered spherical nanoparticles (70 nm diameter), while b-SiO2 nanopowder synthesized from red RHA (S2) and b-SiO2 nanopowder synthesized from brown RHA (S3) were purely spherical (20 nm and 10 nm diameter, respectively). Compared to the S1 (11.36 m2g-1) and S2 (234.93 m2g-1) nanopowders, the S3 nanopowders showed the highest surface area (280.16 m2g-1) due to the small particle size and high porosity. The core level of the X-ray photoelectron spectroscopy (XPS) spectra showed that Si was constituted by two components, Si 2p (102.2 eV) and Si 2s (153.8 eV), while Oxygen 1s was observed at 531.8 eV, confirming the formation of SiO2. The anti-bacterial activity of the b-SiO2 nanopowders was investigated using both gram-positive (Escherichia coli) and gram-negative (Staphylococcus aureus) microorganisms. Compared to S2 and S3 silica nanopowders, S1 demonstrated enhanced antibacterial activity. This study signifies the medical, biomedical, clinical, and biological importance and application of RHA-mediated synthesized b-SiO2.