ABSTRACT
BACKGROUND: Stents coated with amorphous hypothrombogenic silicon carbide (a-SiC:H) have low restenosis rates in humans. Recurrence in a-SiC:H at mid-term follow-up has been shown to be similar to a stainless steel device. The long-term outcome, however, may be different. METHODS: Four hundred ninety-seven patients (63.4 +/- 9.8 years of age) received either the a-SiC:H-coated Tenax stent (Biotronik, Berlin, Germany) or the 316L Nir stent (Boston Scientific, Maple Grove, Minn). Lesions had to be covered with one stent only (diameter > or =2.8 mm, length <20 mm). Exclusion criteria comprised acute myocardial infarction and angiographic thrombus within the target vessel. Twenty-five of 497 (5%) patients were excluded for protocol violation. Clinical follow-up was completed in 450 of 472 (95.3%) and angiographic follow-up was completed in 365 of 472 (77.3%); 22 of 472 (4.7%) patients were lost to follow-up. RESULTS: Major adverse coronary events occurred in 28 of 233 (12%) of the Tenax recipients and in 31 of 217 (14.3%) of the Nir recipients (P =.50). Acute myocardial infarctions were less frequent in the Tenax recipients after > or =60 weeks. Premature target lesion revascularization was performed in 16 of 233 (6.9%) patients in the Tenax group and 11 of 217 (5.1%) (P =.54) patients in the Nir group. Coronary bypass operations were similar after Tenax or Nir stent deployment (3/233 [1.3%] vs 6/217 [2.8%], P =.43), as were deaths in 7 of 233 (3%) versus 8 of 217 (3.7%) (P =.88), respectively. CONCLUSIONS: Both stents had a low rate of major adverse coronary events at 81 +/- 12 weeks of follow-up, with no definite superiority of any of the devices.