ABSTRACT
This study compares the workability, mechanical, and thermal characteristics of structural self-compacting lightweight concrete (SCLWC) formulations using pumice aggregate (PA), expanded perlite aggregate (EPA), fly ash (FA), and silica fume (SF). FA and SF were used as partial substitutes for cement at a 10% ratio in various mixes, impacting different aspects: According to the obtained results, FA enhanced the workability but SF reduced it, while SF improved the compressive and splitting tensile strengths more than FA. EPA, used as a fine aggregate alongside PA, decreased the workability, compressive strength, and splitting tensile strength compared to the control mix (K0). The thermal properties were altered by FA and SF similarly, while EPA notably reduced the thermal conductivity coefficients. The thermal conductivity coefficients (TCCs) of the K0-K4 SCLWC mixtures ranged from 0.275 to 0.364 W/mK. K0 had a TCC of 0.364 W/mK. With 10% FA, K1 achieved 0.305 W/mK; K2 with 10% SF reached 0.325 W/mK. K3 and K4, using EPA instead of PA, showed significantly lower TCC values: 0.275 W/mK and 0.289 W/mK, respectively. FA and SF improved the thermal conductivity compared to K0, while EPA further reduced the TCC values in K3 and K4 compared to K1 and K2. The compressive strength (CS) values of the K0-K4 SCLWC mixtures at 7 and 28 days reveal notable trends. Using 10% FA in K1 decreased the CS at both 7 days (12.16 MPa) and 28 days (22.36 MPa), attributed to FA's gradual pozzolanic activity. Conversely, K2 with SF showed increased CS at 7 days (17.88 MPa) and 28 days (29.89 MPa) due to SF's rapid pozzolanic activity. Incorporating EPA into K3 and K4 reduced the CS values compared to PA, indicating EPA's lower strength contribution due to its porous structure.
ABSTRACT
Cement production in the world market is steadily increasing. In 2000, it was 1600 million tons, while as of 2013, the annual amount exceeded 4000 million tons. The burning of cement clinker is associated with the generation of waste. It is estimated that the amount of cement kiln dust (CKD), during combustion, reaches about 15-20%, which means 700 million tons per year. However, not all types of by-products are reusable due to high alkali, sulfate, and chloride contents, which can adversely affect the environment. One environmentally friendly solution may be to use CKD in the production of high-performance concrete (HPC), as a substitute for some of the cement. This paper presents a study of the short- and long-term physical and mechanical properties of HPC with 5%, 10%, 15%, and 20% CKD additives. The experiments determined density, water absorption, porosity, splitting tensile strength, compressive strength, modulus of elasticity, ultrasonic pulse velocity, and evaluated the microstructure of the concrete. The addition of CKD up to 10% caused an increase in the 28- and 730-day compressive strengths, while the values decreased slightly when CKD concentration increased to 20%. Splitting tensile strength decreased proportionally with 5-20% amounts of CKD regardless of HPC age. Porosity, absorbability, and ultrasonic pulse velocity decreased with increasing cement dust, while the bulk density increased for HPC with CKD. Microstructure analyses showed a decrease in the content of calcium silicate hydrate (C-S-H), acceleration of setting, and formation of wider microcracks with an increase in CKD. From the results, it was shown that a 15% percentage addition of CKD can effectively replace cement in the production of HPC and contribute to reducing the amount of by-product from the burning of cement clinker.
ABSTRACT
The goal of this paper is to investigate the impact of nano-materials on the mechanical and electrochemical properties of self-cleaning concrete. Nano-titanium dioxide and nano-zinc oxide were used as additives for this purpose. Additionally, a comparative study on the effect of using these materials on the self-cleaning concrete's characteristics was conducted. The dosages of nano-titanium dioxide (nps-TiO2) and nano-zinc oxide (nps-ZnO) used were 0, 0.5, 1, 1.5, 2, and 2.5% and 0, 1, 2, and 3% of the weight of the cement, respectively. The results showed that the optimum compressive strength and the lowest corrosion rate were fulfilled at 2.5% of nps-TiO2 and 1% of nps-ZnO, and using 2.5% of nps-TiO2 achieved the highest improvement in the corrosion rate. However, 1% for nps-TiO2 mixtures and 1% for nps-ZnO mixtures were the best ratios for flexural strength. On the other hand, for the corrosion rate, the samples were tested at 2 and 6 months. When nps-TiO2 and nps-ZnO samples were compared to the control sample, 2.5% and 1% of nps-TiO2 and nps-ZnO, respectively, showed the largest improvement in resistance to corrosion. Also, the self-cleaning property of the samples containing nano-materials (nps-TiO2 and nps-ZnO) was tested. As the results illustrated, the self-cleaning property of the samples was increased over time due to photocatalytic degradation. Furthermore, the results of the photocatalytic tests showed that nps-TiO2 samples outperformed nps-ZnO samples overall.
ABSTRACT
Fracture characteristics were used to effectively evaluate the performance of fiber-reinforced cementitious composites. The fracture parameters provided the basis for crack stability analysis, service performance, safety evaluation, and protection. Much research has been carried out in the proposed study field over the previous two decades. Therefore, it was required to analyze the research trend from the available bibliometric data. In this study, the scientometric analysis and science mapping techniques were performed along with a comprehensive discussion to identify the relevant publication field, highly used keywords, most active authors, most cited articles, and regions with largest impact on the field of fracture properties of cement-based materials (CBMs). Furthermore, the characteristic of various fibers such as steel, polymeric, inorganic, and carbon fibers are discussed, and the factors affecting the fracture properties of fiber-reinforced CBMs (FRCBMs) are reviewed. In addition, future gaps are identified. The graphical representation based on the scientometric review could be helpful for research scholars from different countries in developing research cooperation, creating joint ventures, and exchanging innovative technologies and ideas.
ABSTRACT
This study investigates the fracture properties of high performance cementitious composites (HPCC) with four different types of fibres and with volume fraction content 3%. The four fibres are steel hooked end (S), polypropylene crimped (PP), basalt chopped (B), and glass (G) fibres. The tests were carried out in accordance with the RILEM recommendations. In order to examine the fresh properties of HPCC the slump flow tests were performed. Twelve fibre reinforced HPCC beam specimens with notch were cast and tested using central point loading experiments. In addition, experimental tests of the compressive strength and splitting tensile strength were carried out. The test results made it possible to obtain representative fracture parameters, such as the equivalent strengths, residual strengths, and fracture energy of fibre reinforced HPCC. The S fibre specimens showed the best performance in terms of workability, compressive strength, tensile splitting strength, and fracture energy at large deflection. On the other hand, G fibre specimens exhibited the best performance in terms of flexural strength, equivalent flexural strength at higher deflection, and residual flexural strength at lower deflection. In terms of equivalent flexural strength at lower deflection and residual flexural strength at higher deflection, basalt fibre specimens performed the best. On the contrary, polypropylene fibre reinforced beam specimens revealed the highest deflection capacity.
ABSTRACT
This study has investigated the changes that might appear in post-peak flexural response. Before the flexural test, prismatic specimens were placed in a furnace chamber and exposed to elevated temperatures of 400, 600, and 800 °C. The flexural toughness test was carried out on two types of concrete: Plain ultra-high performance concrete (UHPC) and UHPC with different types of fibres (steel fibre (SF) and polypropylene fibre (PPF)) at 0.5%, 1%, 1.5%, and 2% volume fractions. During the flexural test in the macro-crack development analysis, the non-contact ARAMIS system was used to perform three-dimensional measurements of strain and displacement. The results of scanning electron microscope (SEM) observations of micro-crack development in UHPC without and with SF/PPF were also presented. The experimental results showed that in some cases, the load-deflection curve of fibre-reinforced UHPC displayed a double-peak response. The first peak signified the UHPC properties, while the second peak represented the properties of the fibres. Under flexural load, the toughness decreased as the temperature increased. Significant decrease in the load-deflection response and toughness were observed for the polypropylene fibre-reinforced UHPC when the temperature approached 800 °C. The SEM observation results showed that the thermal damage of fibre-reinforced UHPC depends on the pore pressure effect, the thermal mismatch, the decomposition of hydration products, and the formation of micro-cracks.
ABSTRACT
The article presents the results of experimental- and analytical investigations of the behaviour and the load-carrying capacity of deep beams with openings (DBO) and without openings (DB) made of hybrid steel-polypropylene fibre-reinforced high-performance concrete (HFRHPC) subjected to three-point bending tests. Six deep beams 100 mm × 500 mm × 1000 mm were tested with a gradually increasing load until failure. All the specimens were tested in the same simply supported conditions. The research focused on the quantity and kind of concrete reinforcement. The deep beams with steel and polypropylene (PP) fibres were characterised by variously arranged steel bar reinforcement: vertically, horizontally, orthogonally and diagonally. The DB1, DBO1 deep beams were conventionally made with steel rod reinforcement but without fibres. The steel wire mesh reinforcement was replaced by fibre reinforcement of varying volume percentages in the remaining deep beams. The influence of the hybrid fibre content in the specimens was studied by marking the development and propagation of cracks, by recording the failure modes, and by monitoring the deflections at the bottom of the deep beam, at the mid-span and at the support. Three-dimensional measurements of strain and displacement of the deep beams without openings (DB) were performed by the non-contact optical 3D deformation measuring system ARAMIS. The experimental results were compared with the studied methods of predicting the shear strength of deep beams reinforced with hybrid fibre. The conducted study demonstrates that hybrid fibres as web reinforcement have a favourable impact on deep beam crack widths and raise the load carrying capacity of deep beams with openings.