ABSTRACT
A cycle of works on manufacturing and studying laser and magnetooptical ceramics with a focus on their thermo-optical characteristics performed by the research team is analyzed. Original results that have not been published before such as measurements of the Verdet constant in the Zr:TAG, Re:MgAl2O4, and ZnAl2O4 ceramics are also presented.
ABSTRACT
Thermally induced depolarization of radiation introduced by a system of two optical elements separated by a quartz rotator has been analyzed. The conditions of full compensation of thermally induced depolarization for two nonidentical optical elements have been found. The model experiment has demonstrated that full compensation in two optical elements of different materials is possible without a quartz rotator between them.
ABSTRACT
Thermally induced depolarization and thermal lens of three Konoshima Chemical Co. laser-ceramics samples Yb(3+):Lu(2)O(3)(C(Yb) ≈ 1.8 at.%), Yb(3+):Y(2)O(3)(C(Yb) ≈ 1.8 at.%), and Yb(3+):Sc(2)O(3) (C(Yb) ≈ 2.5 at.%) were measured in experiment at different pump power. The results allowed us to estimate the thermal conductivity of the investigated ceramic samples and compare their thermo-optical properties. The thermo-optical constants P and Q and its sign measured for these materials at the first time.
ABSTRACT
Compensation of thermally induced depolarization in laser active elements at small birefringence without additional phase elements was proposed and observed experimentally. Requirements to the crystals were formulated. An order of magnitude reduction of depolarization degree was obtained experimentally. A further modification of the scheme was developed.