ABSTRACT
Additive manufacturing (AM), also known as 3D printing, offers many advantages and, particularly in the medical field, it has stood out for its potential for the manufacture of patient-specific implantable devices. Thus, the unique properties of 3D-printed biocompatible polymers such as Polylactic Acid (PLA) and Polyetheretherketone (PEEK) have made these materials the focus of recent research where new post-processing and joining techniques need to be investigated. This study investigates the weldability of PLA and PEEK 3D-printed plates through stationary shoulder friction stir welding (SS-FSW) with assisted heating. An SS-FSW apparatus was developed to address the challenges of rotating shoulder FSW of thermoplastics, with assisted heating either through the shoulder or through the backing plate, thus minimizing material removal defects in the welds. Successful welds revealed that SS-FSW improves surface quality in both PLA and PEEK welds compared to rotating shoulder tools. Process parameters for PLA welds are investigated using the Taguchi method, emphasizing the importance of lower travel speeds to achieve higher joint efficiencies. In PEEK welds, the heated backing plate proved effective in increasing process heat input and reducing cooldown rates which were associated with higher crystallinity PEEK. Despite these findings, further research is needed to improve the weld strength of SS-FSW with these materials considering aspects like tool design, process stability, and 3D printing parameters. This investigation emphasizes the potential of SS-FSW in the assembly of thermoplastic materials, offering insights into the weldability of additively manufactured biocompatible polymers like PLA and PEEK.
ABSTRACT
Polyetheretherketone (PEEK) is the leading high-performance thermoplastic biomaterial that can be processed through material extrusion (ME) additive manufacturing (AM), also known as three-dimensional (3D) printing, for patient-specific load-bearing implant manufacture. Considering the importance of cyclic loading for load-bearing implant design, this work addresses the high-cycle fatigue behaviour of 3D-printed PEEK. In this work, printed PEEK specimens are cyclically loaded under stress-controlled tension-tension using different stress levels between 75% and 95% of printed PEEK's tensile strength. The experimental results are used to document 3D-printed PEEK's fatigue behaviour using Basquin's power law, which was compared with previous fatigue research on bulk PEEK and other 3D-printing materials. As a pioneering study on its fatigue behaviour, the results from this work show that 3D-printed PEEK exhibits an above-average fatigue strength of 65 MPa, corresponding to about 75% of its tensile strength. Fracture surface analysis suggests that a transition can occur from ductile to brittle fracture with maximum stresses between 85% and 95% of the tensile strength. Evidence of crack propagation features on fracture surfaces under scanning electron microscope (SEM) observation suggests crack initiation in void defects created by printing deposition that propagates longitudinally through line bonding interfaces along layers. Considering this, 3D-printed PEEK's fatigue behaviour can be strongly related to printing conditions. Further research on the fatigue behaviour of 3D-printed PEEK is necessary to support its use in load-bearing implant applications.
