ABSTRACT
In this work, the effect of controlled thermal treatment to tune biochar surface properties such as area/porosity, functionalities and reactivity was investigated. TG-MS, CHN, Raman, IR, BET, Zeta and SEM analyses suggested that thermal treatment led to the decomposition of an organic complex/amorphous phase to produce micropores based on graphene nanostructures and a strong increase on surface area from 3m2g-1 for biochar to 30, 408 and 590m2g-1, at 400, 600 and 800°C, respectively. The treatment also led to a gradual decrease on oxygen content from 27 to 14wt% at 800°C due to decomposition of surface functionalities changing surface properties such as zeta potential, adsorption of anionic and cationic species and an increase on the activity for sulfide oxidation which is discussed in terms of increase in surface area and the presence of surface redox quinone groups.
Subject(s)
Charcoal , Adsorption , Graphite , Surface PropertiesABSTRACT
This work describes the synthesis, characterization, and application of an active heterogeneous photo-Fenton system obtained from two different wastes, i.e., laterite (an iron mining waste) and the acid aqueous fraction (AAF) from bio-oil production. AAF with high acidity (ca. 3 molH+ L-1) and organic concentration (25 wt.%) obtained from biomass flash pyrolysis was used for the efficient extraction of Fe3+ from laterite waste. After extraction, the mixture Fe3+/AAF was dried and treated at different temperatures, i.e., 500, 650, and 800 °C, to obtain Fe/C reactive composites. Mössbauer, XRD, TG, elemental analyses, and SEM/EDS showed the presence of highly disperse Fe oxide nanoparticles at 500 and 650 °C and Fe0 particles in the material obtained at 800 °C with carbon contents varying from 74 to 80 %. The three composites were tested as heterogeneous catalysts in the photo-Fenton reaction for the oxidation of the model dye contaminant methylene blue, showing high activities at neutral pH.