A high-capacity, high-power organic electrode via supercritical CO2 impregnation into activated carbon micropores.

Herein, we report the impregnation of chloranil into activated carbon micropores using scCO2. The sample prepared under 105 °C and 15 MPa showed a specific capacity of 81 mAh gelectrode-1, except for the electric double layer capacity at 1 A gelectrode-Polytetrafluoroethylene (PTFE)-1. Additionally, approximately 90% of the capacity was retained even at 4 A gelectrode-PTFE-1.

Series module of quinone-based organic supercapacitor (> 6 V) with practical cell structure.

Inexpensive, high-performing, and environmentally friendly energy storage devices are required for smart grids that efficiently utilize renewable energy. Energy storage devices consisting of organic active materials are promising because organic materials, especially quinones, are ubiquitous and usually do not require harsh conditions for synthesis, releasing less CO2 during mass production. Although fundamental research-scale aqueous quinone-based organic supercapacitors have shown excellent energy storage performance, no practical research has been conducted. In this study, we aimed to develop a practical-scale aqueous-quinone-based organic supercapacitor. By connecting 12 cells of size 10 cm × 10 cm × 0.5 cm each in series, we fabricated a high-voltage (> 6 V) aqueous organic supercapacitor that can charge a smartphone at a 1 C rate. This is the first step in commercializing aqueous organic supercapacitors that could solve environmental problems, such as high CO2 emissions, air pollution by toxic metals, and limited electricity generation by renewable resources.

S/N Co-Doped Hollow Carbon Particles for Oxygen Reduction Electrocatalysts Prepared by Spontaneous Polymerization at Oil-Water Interfaces.

We herein report that sulfur and nitrogen co-doped hollow spherical carbon particles can be applied to oxygen reduction reaction (ORR) electrocatalysts prepared by calcination of polydopamine (PDA) hollow particles. The hollow structure of PDA was formed by auto-oxidative interfacial polymerization of dopamine at the oil and water interface of emulsion microdroplets. The PDA was used as the nitrogen source as well as a platform for sulfur-doping. The obtained sulfur and nitrogen co-doped hollow particles showed a higher catalytic activity than that of nonsulfur-doped particles and nonhollow particles. The high ORR activity of the calcined S-doped PDA hollow particles could be attributed to the combination of nitrogen and sulfur active sites and the large surface areas owing to a hollow spherical structure.