ABSTRACT
A compact advanced extreme-ultraviolet (EUV) spectrometer operating in the EUV wavelength range of a few nanometers to measure spatially resolved line emissions from tungsten (W) was developed for studying W transport in fusion plasmas. This system consists of two perpendicularly crossed slits-an entrance aperture and a space-resolved slit-inside a chamber operating as a pinhole, which enables the system to obtain a spatial distribution of line emissions. Moreover, a so-called v-shaped slit was devised to manage the aperture size for measuring the spatial resolution of the system caused by the finite width of the pinhole. A back-illuminated charge-coupled device was used as a detector with 2048 × 512 active pixels, each with dimensions of 13.5 × 13.5 µm2. After the alignment and installation on Korea superconducting tokamak advanced research, the preliminary results were obtained during the 2016 campaign. Several well-known carbon atomic lines in the 2-7 nm range originating from intrinsic carbon impurities were observed and used for wavelength calibration. Further, the time behavior of their spatial distributions is presented.
ABSTRACT
The interfacial properties were systematically investigated using an organic sensitizer (3-(5'-{4-[(4-tert-butyl-phenyl)-p-tolyl-amino]-phenyl}-[2,2']bithiophenyl-5-yl)-2-cyano-acrylic acid (D)) and inorganic sensitizer (bis(tetrabutylammonium) cis-bis(thiocyanato)bis(2,2'-bipyridine-4,4'-dicarboxylato) ruthenium(II) (N719)) in a liquid-state and a solid-state dye-sensitized solar cell (DSC). For liquid-DSCs, the faster charge recombination for the surface of D-sensitized TiO2 resulted in shorter diffusion length (LD) of â¼3.9 µm than that of N719 (â¼7.5 µm), limiting the solar cell performance at thicker films used in liquid-DSCs. On the other hand, for solid-DSCs using thin TiO2 films (â¼ 2 µm), D-sensitized device outperforms the N719-sensitized device in an identical fabrication condition, mainly due to less perfect wetting ability of solid hole conductor into the porous TiO2 network, inducing the dye monolayer act as an insulation layer, while liquid electrolyte is able to fully wet the surface of TiO2. Such insulation effect was attributed to the fact that the significant increase in recombination resistance (from 865 to 4,400 Ω/cm(2)) but shorter electron lifetime (from 10.8 to 0.8 ms) when compared to liquid-DSCs. Higher recombination resistance for solid-DSCs induced the electron transport-limited situation, showing poor performance of N719-sensitized device which has shorter electron transport time and similar LD (2.9 µm) with D-sensitized device (3.0 µm).