ABSTRACT
In this report, emplectite (CuBiS2) semiconductor has been deposited on mesoporous TiO2 using gas-solid reaction method. For the first time, CuCl2 and BiCl3 are solution-coated on mesoporous TiO2 films, and thereafter reacted with H2S gas in an H2S atmosphere. The CuBiS2 film is further confirmed using X-ray diffraction; thus, demonstrating the pure phase of CuBiS2. CuBiS2 film shows high spectral absorption with an energy gap (Eg) of 2.18 eV. Furthermore, devices have a structure consisting of FTO/compact-TiO2/mesoporous-TiO2/CuBiS2/P3HT/Ag have been fabricated and hence exhibit high photoresponse performance.
ABSTRACT
The perovskite CH3NH3PbI3 was prepared on a mesoscopic TiO2 film, starting from electrodepositing PbO, to iodination to PbI2, and then interdiffusion reaction with CH3NH3I. The as-prepared film was used as a light absorber for the perovskite solar cells, exhibiting a high PCE of 12.5% under standard AM 1.5 conditions.
ABSTRACT
A panchromatic dye was synthesized with an isoindigo core as a linker to bridge with a bis(4-tert-butylphenyl)phenylamine donor and a cyanoacetic acid acceptor for dye-sensitized solar cells, showing a broad spectral response and a high conversion efficiency of 7.55% under AM 1.5 conditions.
ABSTRACT
Two D-pi-A conjugated molecules, BzTCA and BzTMCA, were developed through facile synthetic approaches for dye-sensitized solar cells. The investigation of the photophysical properties of BzTCA and BzTMCA both in dilute solutions and in thin films indicates that their absorption exhibits a wide coverage of the solar spectrum. The absorption features for BzTCA and BzTMCA commence at about 710 nm in solution, and at about 800 nm in the solid state. The absorption maxima (lambda(max)) for both BzTCA and BzTMCA on TiO(2) film are almost the same as those in dilute solution. Their HOMOs and LUMOs were found to partly overlap at the center of these dyes, which guarantees appreciable interactions between the donors and acceptors. The investigation of the performance of dye-sensitized solar cells fabricated from BzTCA and BzTMCA indicated that the power-conversion efficiencies are 6.04 % and 4.68 %, respectively, which could be comparable with the normal sensitizer N3. BzTMCA showed lower incident photon-to-electron conversion efficiency (IPCE) and J(sc) values relative to BzTCA, which is probably because of the weaker driving force of dye regeneration and electron injection process of BzTMCA. The IPCE responsive area reached nearly 800 nm, which provides great potential for further improvement of the photocurrent density and power-conversion efficiency. Our investigations demonstrate that both dyes BzTCA and BzTMCA could be promising candidates for dye-sensitized solar cells.
ABSTRACT
The catalytic enantioselective synthesis of all-carbon quaternary stereogenic centers in spirocyclic diketones has been achieved for the first time by an unprecedented asymmetric vinylogous alpha-ketol rearrangement in which an enantiocontrolled semipinacol-type 1,2-carbon migration was realized using multifunctional cinchona-modified primary amine catalysis.