ABSTRACT
Silver metallization pastes for crystalline silicon PV cells containing nanosized metallic zinc were found to be superior to commercial pastes containing micrometer-sized metallic zinc and micrometer sized zinc oxide in terms of efficiency and firing window. Efficiency performance decreases as the size of the particles increases: nano-Zn > 3.6 µm Zn > 4.4 µm Zn. Advanced electron microscopy techniques were used to investigate the interfacial microstructure between the front-side contact and the Si emitter of nanosized zinc additive based cells fired at temperatures from below to above optimal. These microstructural observations confirmed the possibility of a tunneling mechanism of current flow (a "nano-Ag colloid assisted tunneling" model) in the absence of Ag crystallites. Contact resistance maps were used to guide sampling, leading to a better understanding of the relationship between microstructure and contact resistance. Low contact resistance and higher cell efficiency, especially at under- and overfiring temperature conditions, are due to more uniform silicon nitride etching obtained through the use of nanosized metallic zinc additives.