ABSTRACT
AIM AND OBJECTIVES: This study aims to determine the effect on shear bond strength (SBS) and adhesive remnant score between two color change adhesives (CCAs) with reduced curing time using different high-intensity light emitting diode (LED) units. MATERIALS AND METHODS: A total of 108 human first maxillary premolar teeth were randomly allocated into three principal groups (n = 36) based on the type of adhesives used. The adhesives include two CCAs: Transbond Plus Color Change Adhesive (3M, St. Paul, MN, USA) and Grengloo (Ormco, Orange, CA, USA), and the conventional tooth-colored adhesive: Transbond XT (3M). Each principal group was further divided into three sub-groups (n = 12 each) based on the curing time and type of high-intensity LED units used for bonding the stainless steel brackets. Woodpecker iLED Light Curing Unit (Guilin Woodpecker Medical Instrument Co., Ltd., Guilin, China) was cured for three and six seconds, and the ELIPAR S10 LED Curing Light (3M) was cured for 20 seconds. Bonding of the brackets was done in a standardized manner following the manufacturers' instructions. All the samples were submerged in distilled water at 370C for 24 hours. SBS testing was performed using an Instron machine, and adhesive residue on the debonded surface was examined and scored using a stereomicroscope. Statistical analysis was conducted using one-way ANOVA and Tukey's post-hoc test. RESULTS: The results showed significant differences in SBS based on curing time and the type of adhesive resin used. The six seconds curing group exhibited the higher SBS values (15.5 - 22.82 Megapascals [MPa]) followed by the 20 seconds (12.17 - 18.14 MPa) and three seconds (11.31 - 11.74 MPa) groups. Grengloo adhesive demonstrated the highest SBS values among the three types of adhesives. The predominant adhesive remnant scores were 2 and 3. CONCLUSIONS: Grengloo adhesive demonstrates superior bond strength compared to Transbond Plus and Transbond XT. Both Transbond Plus and Grengloo adhesives experience bond failure within the adhesive layer, regardless of the curing intensity or time.