ABSTRACT
BACKGROUND: Conventional sintering methods of dental ceramics have limitations of high temperature and slow cooling rates with requirements of additional heat treatment for crystallization. Spark plasma sintering (SPS) is an emerging technique that has the potential to process dental restorations with dense microstructures and tailor-made clinically relevant properties with optimized processing parameters. This study explored the potential of the SPS of zirconia-reinforced fluormica glass (FM) for dental restorative materials. METHODS: FM glass frit was obtained through the melt-quench technique (44.5 SiO2-16.7 Al2O3-9.5 K2O-14.5 MgO-8.5 B2O3-6.3 F (wt.%)). The glass frit was ball-milled with 20 wt.% of 3 mol% yttria-stabilized zirconia (FMZ) for enhanced fracture toughness. The mixtures were SPS sintered at a pressure of 50 MPa and a heating rate of 100 °C/min for 5 min with an increase in temperature from 650-750 °C-850 °C-950 °C. Phase analysis was carried out using XRD and microstructural characterization with SEM. Micro-hardness, nano-indentation, porosity, density, indentation fracture toughness, and genotoxicity were assessed. CONCLUSIONS: The increase in the SPS temperature of FMZ influenced its microstructure and resulted in reduced porosity, improved density, and optimal mechanical properties with the absence of genotoxicity on human gingival fibroblast cells.
ABSTRACT
We report on the simple, single-step, and cost-effective fabrication, characterization, and performance evaluation of cobalt ferrite (CoFe2O4; CFO) nanocrystalline (NC) thin films on a flexible mica substrate. The chemical solution-based drop-casting method employed to fabricate crystalline CFO films and their characterization was performed by studying the phase formation, surface morphology, and magnetic parameters, while sensor applicability was evaluated using combined magnetic and magnetostrictive properties. X-ray diffraction (XRD) indicates the single-phase and nanocrystalline nature of CFO films, where the crystallite size is â¼60 nm. The optimum conditions employed resulted in CFO NC films with surface particles exhibiting a spherical shape morphology with a homogeneous size distribution, as revealed by scanning electron microscopy analyses. Raman spectroscopic characterization of the chemical bonding indicates all of the active bands that are characteristic of the ferrite phase confirm the spinel structure, which is in agreement with XRD studies. The saturation magnetization (M S) and coercivity (H C), which are extracted from the field-dependent magnetization data, of CFO NC films were found to be 15.8 emu/g and 1.6 kOe, respectively, while the first-order magnetocrystalline anisotropy constant K 1 was â¼1.07 × 106 erg/cm3. The magnetostriction strain curve indicates that the CFO NC films exhibit a strain value of â¼86 ppm at an applied magnetic field of 8 kOe, indicating their suitability for flexible sensor devices.