Two-year Effects of Chlorhexidine-containing Adhesives on the In Vitro Durability of Resin-dentin Interfaces and Modeling of Drug Release.

OBJECTIVES: To evaluate the effects of addition of diacetate chlorhexidine (CHX) at different concentrations into two etch-and-rinse adhesive systems on CHX release, as well as the immediate (IM) and two-year (2-Y) resin-dentin microtensile bond strength (µTBS) and nanoleakage (NL). METHODS: CHX was added to XP Bond (XP) and Ambar (AM) at concentrations of 0.0 wt% (control); 0.01 wt%; 0.05 wt%; and 0.1 to 0.2 wt%. To assess the cumulative CHX release, adhesive disks were made in a metallic matrix and after light-curing were stored in water. Ultraviolet spectrophotometric measurements of the storage solution were performed to examine the release kinetics of CHX. For µTBS and NL, the occlusal enamel of molars was removed and the adhesives were applied to the dentin surface after acid etching. After composite resin build-up, specimens were sectioned to obtain µTBS sticks. The specimens were subjected to µTBS and NL at IM and after 2-Y. In addition, specimens underwent examination for CHX using micro-Raman spectroscopy. All data were submitted to statistical analysis (α=0.05). RESULTS: With regard to CHX release, AM showed a slower and gradual release of CHX while XP released CHX more quickly ( p<0.05), and CHX was still present in the hybrid layers after 2-Y. Both adhesives showed CHX release at 2-Y water storage. Both CHX-containing adhesives showed higher µTBS values than did the control group ( p<0.05).

Effect of acidity of in-office bleaching gels on tooth sensitivity and whitening: a two-center double-blind randomized clinical trial.

OBJECTIVES: The study aimed to compare the tooth sensitivity (TS) and bleaching efficacy of two hydrogen peroxide gels with different pHs (acid pH [Pola Office, SDI] and the neutral pH [Pola Office+, SDI]) used for in-office bleaching. MATERIALS AND METHODS: Fifty-four patients from Brazil and Chile, with right superior incisor darker than A2, were selected for this double-blind, split-mouth randomized trial. Teeth were bleached in two sessions, with 1-week interval. Each session had three applications of 8 min each, according to the manufacturer's instructions. The color changes were evaluated by subjective (Vita Classical and Vita Bleachedguide) and objective (Easy shade spectrophotometer) methods. Participants recorded TS with 0-10 visual analog scale. Color change in shade guide units (SGU) and ΔE was analyzed by Student's t test (α = 0.05). The absolute risk and intensity of TS were evaluated by McNemar's test and Wilcoxon-paired test, respectively (α = 0.05). RESULTS: All groups achieved the same level of whitening after 30 days of clinical evaluation. The use of a neutral in-office bleaching gel significantly decreases the absolute risk of TS (28%, 95% CI 18-41) and intensity of TS when compared to the acid bleaching gel (absolute risk of 50%, 95% CI 37-63). CONCLUSION: The use of a neutral in-office bleaching agent gel produced the same whitening degree than an acid bleaching gel but with reduced risk and intensity of tooth sensitivity. CLINICAL SIGNIFICANCE: Clinicians should opt to use in-office bleaching with a neutral gel than an acid product because the former causes a significant lower risk and intensity of tooth sensitivity.

Effect of Minocycline on the Durability of Dentin Bonding Produced with Etch-and-Rinse Adhesives.

OBJECTIVES: To evaluate the effect of minocycline and chlorhexidine pretreatment of acid-etched dentin on the longevity of resin-dentin bond strength (µTBS) and nanoleakage of two-step etch-and-rinse adhesives. METHODS: Before application of Prime & Bond NT and Adper Single Bond 2 in occlusal dentin, the dentin surfaces were treated with 37% phosphoric acid, rinsed, air-dried, and rewetted with water (control group), 2% minocycline, or 2% chlorexidine digluconate. Composite buildups were constructed incrementally, and specimens were longitudinally sectioned to obtain bonded sticks (0.8 mm2) to be tested in tension (0.5 mm/min) immediately or after 24 months of water storage. For nanoleakage, two specimens of each tooth/period were immersed in the silver nitrate solution, photo-developed, and polished with SiC paper for analysis under energy-dispersive X-ray spectroscopy/scanning electron microscopy. RESULTS: Reductions of the µTBS and increases in the nanoleakage were observed for both adhesives when the rewetting procedure was performed with water. Stable bonds were observed for the 2% minocycline and 2% chlorexidine digluconate groups after 24 months. CONCLUSIONS: The use of 2% minocycline as pretreatment of acid-etched dentin is one alternative to retard the degradation of resin-dentin interfaces over a 24-month period as well as 2% chlorexidine digluconate.

Chlorhexidine-containing acid conditioner preserves the longevity of resin-dentin bonds.

The current study evaluated the effect of 2% chlorhexidine digluconate (CHX) on the immediate and six-month resin-dentin bond strength (BS) and nanoleakage pattern (NL) of etch-and-rinse adhesives when applied in aqueous or associated to the phosphoric acid conditioner. The occlusal enamel of 42 caries-free extracted molars was removed in order to expose a flat dentin surface. In groups 1 and 2 (control-C), the surfaces were acid etched with conventional phosphoric acid, and the adhesives Prime&Bond NT (PB) and Adper Single Bond 2 (SB) were applied after rinsing, drying and rewetting with water. In groups 3 and 4 (Ac/CHX), the adhesives were applied in a similar manner, however, a 2% CHX-containing acid was previously applied. In groups 5 and 6 (CHX), the adhesives were applied according to the control group; however, the rewetting procedure was performed with an aqueous solution of 2% CHX for 60 seconds. Composite buildups (Opallis, FGM) were constructed incrementally, and the specimens were longitudinally sectioned in the "x" and "y" directions to obtain bonded sticks (0.8 mm2) to be tested in tension at 0.5 mm/minute immediately or after six months of water storage. For NL, two bonded sticks from each tooth were coated with nail varnish, placed in silver nitrate and polished down with SiC paper. Resin-dentin interfaces were analyzed by EDX-SEM. The BS and NL data from each adhesive was submitted to two-way repeated measures ANOVA and Tukey's test (alpha=0.05). After six months of water storage, significant reductions in BS were observed for both adhesives in the control group (p<0.05). When Ac/CHX or CHX was used, no significant reductions in BS were observed for both systems. Nanoleakage was more evident in the control group than in the experimental groups (p<0.05), even after six months. The use of CHX in an aqueous solution or associated with the acid conditioner was effective for reducing degradation of resin-dentin bonds after six months of water storage.