Structural insight into the magnesium borohydride - ethylenediamine solid-state Mg-ion electrolyte system.

A highly complex crystal structure of stoichiometric Mg5(en)6(BH4)10 was solved from single crystal synchrotron X-ray diffraction and confirmed by neutron powder diffraction (NPD) on isotopically substituted Mg(en)1.2(11BD4)2. We highlight the role of the amorphous Mg(BH4)2 in the reactivity of the Mg(BH4)2-en system and characterized a previously overlooked phase, Mg(en)2(BH4)2.

High Yield Autoclave Synthesis of pure M2B12H12 (M = Na, K).

Metal dodecaborates (MxB12H12) are a versatile class of materials used in polymer chemistry and cancer treatment and are promising candidates as electrolytes for solid-state batteries. However, a general and scalable approach has not yet been developed for producing high-purity B12H122- derivatives. In this work, we report a simple, efficient, and environmentally benign solvothermal method to prepare diffraction and 11B NMR pure Na2B12H12 (85% yield) and K2B12H12 (84% yield). This new synthetic approach is based on the use of the borane dimethyl sulfide complex (DMS·BH3) and borohydrides (NaBH4, KBH4) heated at different temperatures in diglyme in an autoclave. It was found that high-purity Na2B12H12·diglyme solvate is obtained via an intermediate formation of B3H8-, B9H14-, and B11H14-, which are all soluble in diglyme. Heating under vacuum is shown to be efficient for removing the coordinated diglyme, allowing the formation of unsolvated Na2B12H12. Autoclave synthesis starting from KBH4 directly yields solvent-free K2B12H12, and ball-milling KBH4 prior to the synthesis enabling us to significantly improve the final yield. The new synthetic method paves the way for large-scale synthesis of MxB12H12 derivatives, enabling to envisage a wider scope of practical applications.

Synthesis, Structure, and Thermal Stability of a Mesoporous Titanium(III) Amine-Containing MOF.

The first mesoporous bimetallic TiIII/Al metal-organic framework (MOF) containing amine functionalities on its linkers has been selectively obtained by converting the cheap commercially available (TiCl3)3AlCl3 into Ti3-xAlxCl3(THF)3 and reacting this complex with 2-aminoterephthalic acid in dimethylformamide (DMF) under soft solvothermal conditions. This compound is structurally related to the previously described NH2-MIL-101(M) (M = Cr, Al, and Fe) MOFs. Thermal gravimetric analyses and in situ powder X-ray diffraction (PXRD) measurements demonstrated that this highly air-sensitive TiIII-containing MOF is structurally stable up to 200 °C. Nuclear magnetic resonance (NMR) spectroscopy, elemental analysis, and inductively coupled plasma (ICP) revealed that NH2-MIL-101(TiIII) contains trinuclear Ti3(µ3-O)Cl(DMF)2(RCOO)6 clusters with strongly bound DMF molecules and a small amount of aluminum. Sorption experiments revealed a higher affinity of this MOF for hydrogen compared to the previously described monometallic unfunctionalized MIL-101(TiIII) MOF.

Functionalization of Mono- and Bimetallic MIL-100(Al,Fe) MOFs by Ethylenediamine: Postfunctionalization, Brønsted Acido-Basicity, and Unusual CO2 Sorption Behavior.

The metal sites of MIL-100(Fe), MIL-100(Fe,Al), and MIL-100(Al) metal-organic frameworks (MOFs) were decorated with ethylenediamine (EN). Interestingly, the Al-containing MOFs presented hierarchized porosity, and their structural integrity was maintained upon functionalization. Solution and solid-state NMR confirmed the grafting efficiency in the case of MIL-100(Al) and the presence of a free amine group. It was shown that MIL-100(Al) can be functionalized by only one EN molecule in each trimeric Al3O cluster unit, whereas the other two aluminum sites are occupied by a hydroxyl and a water molecule. The -NH2 sites of the grafted ethylenediamine can be used for further postfunctionalization through amine chemistry and are responsible for the basicity of the functionalized material as well as increased affinity for CO2. Furthermore, the presence of coordinated water molecules on the Al-MOF is responsible for simultaneous Brønsted acidity. Finally, the Al-containing MOFs show an unusual carbon dioxide sorption mechanism at high pressures that distinguishes those materials from their iron and chromium counterparts and is suspected to be due to the presence of polarized Al-OH bonds.

Mechanochemical defect engineering of HKUST-1 and impact of the resulting defects on carbon dioxide sorption and catalytic cyclopropanation.

Metal-organic frameworks (MOFs) are recognized as ideal candidates for many applications such as gas sorption and catalysis. For a long time the properties of these materials were thought to essentially arise from their well-defined crystal structures. It is only recently that the importance of structural defects for the properties of MOFs has been evidenced. In this work, salt-assisted and liquid-assisted grinding were used to introduce defects in a copper-based MOF, namely HKUST-1. Different milling times and post-synthetic treatments with alcohols allow introduction of defects in the form of free carboxylic acid groups or reduced copper(i) sites. The nature and the amount of defects were evaluated by spectroscopic methods (FTIR, XPS) as well as TGA and NH3 temperature-programmed desorption experiments. The negative impact of free -COOH groups on the catalytic cyclopropanation reaction of ethyl diazoacetate with styrene, as well as on the gravimetric CO2 sorption capacities of the materials, was demonstrated. The improvement of the catalytic activity of carboxylic acid containing materials by the presence of CuI sites was also evidenced.

Gravimetric tank method to evaluate material-enhanced hydrogen storage by physisorbing materials.

The most common methods to evaluate hydrogen sorption (volumetric and gravimetric) require significant experience and expensive equipment for providing reproducible results. Both methods allow one to measure excess uptake values which are used to calculate the total amount of hydrogen stored inside of a tank as required for applications. Here we propose an easy to use and inexpensive alternative approach which allows one to evaluate directly the weight of hydrogen inside a material-filled test tank. The weight of the same tank filled with compressed hydrogen in the absence of loaded material is used as a reference. We argue that the only parameter which is of importance for hydrogen storage applications is by how much the material improves the total weight of hydrogen inside of the given volume compared to compressed gas. This parameter which we propose to name Gain includes both volumetric and gravimetric characterization of the material; it can be determined directly without knowing the skeletal volume of the material or excess sorption. The feasibility of the Gravimetric Tank (GT) method was tested using several common carbon and Metal Organic Framework (MOF) materials. The best Gain value of ∼12% was found for the Cu-BTC MOF which means that the tank completely filled with this material stores a 12% higher amount of hydrogen compared to H2 gas at the same P-T conditions. The advantages of the GT method are its inexpensive design, extremely simple procedures and direct results in terms of tank capacity as required for industrial applications. The GT method could be proposed as a standard check for verification of the high hydrogen storage capacity of new materials. The GT method is expected to provide even better accuracy for evaluation of a material's performance for storage of denser gases like e.g. CO2 and CH4.

Synthesis and Catalytic Applications of Multi-Walled Carbon Nanotube-Polyamidoamine Dendrimer Hybrids.

Polyamidoamine (PAMAM) dendrimers were covalently immobilized on multi-walled carbon nanotubes (MWNT) by two "grafting to" strategies. We demonstrate the existence of non-covalent interactions between the two components but outline the superiority of our two grafting approaches, namely xanthate and click chemistry. MWNT surfaces were functionalized with activated ester and propargylic moieties prior to their reaction with PAMAM or azido-PAMAM dendrimers, respectively. The grafting of PAMAM generations 0 to 3 was evaluated with X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), and transmission electron microscopy (TEM). The versatility of our hybrids was demonstrated by post-functionalization sequences involving copper alkyne-azide cycloaddition (CuAAC). We synthesized homogeneous supported iridium complexes at the extremities of the dendrimers. In addition, our materials were used as templates for the encapsulation of Pd nanoparticles (NPs), validating our nanocomposites for catalytic applications. The palladium-based catalyst was active for carbonylative coupling over five consecutive runs without loss of activity.