Multiple Mechanical Gradients are Responsible for the Strong Adhesion of Spider Attachment Hair.

Wandering spiders climb vertically and walk upside-down on rough and smooth surfaces using a nanostructured attachment system on their feet. The spiders are assumed to adhere by intermolecular van der Waals forces between the adhesive structures and the substrate. The adhesive elements are arranged highly ordered on the hierarchically structured attachment hair (setae). While walking, it has been suggested that the spiders apply a shear force on their legs to increase friction. However, the detailed mechanical behavior of the hair's structures during attachment and detachment remains unknown. Here, gradients of the mechanical properties of the attachment hair on different length scales that have evolved to support attachment, stabilize adhesion in contact, and withstand high stress at detachment, examined by in situ experiments, are shown. Shearing helps to self-align the adhesive elements with the substrate. The study is anticipated to contribute to the development of optimized artificial dry adhesives.

Hierarchical architecture of spider attachment setae reconstructed from scanning nanofocus X-ray diffraction data.

When sitting and walking, the feet of wandering spiders reversibly attach to many surfaces without the use of gluey secretions. Responsible for the spiders' dry adhesion are the hairy attachment pads that are built of specially shaped cuticular hairs (setae) equipped with approximately 1 µm wide and 20 nm thick plate-like contact elements (spatulae) facing the substrate. Using synchrotron-based scanning nanofocus X-ray diffraction methods, combining wide-angle X-ray diffraction/scattering and small-angle X-ray scattering, allowed substantial quantitative information to be gained about the structure and materials of these fibrous adhesive structures with 200 nm resolution. The fibre diffraction patterns showed the crystalline chitin chains oriented along the long axis of the attachment setae and increased intensity of the chitin signal dorsally within the seta shaft. The small-angle scattering signals clearly indicated an angular shift by approximately 80° of the microtrich structures that branch off the bulk hair shaft and end as the adhesive contact elements in the tip region of the seta. The results reveal the specific structural arrangement and distribution of the chitin fibres within the attachment hair's cuticle preventing material failure by tensile reinforcement and proper distribution of stresses that arise upon attachment and detachment.