Retention Load of Telescopic Crowns with Different Taper Angles between Cobalt-Chromium and Polyetheretherketone Made with Three Different Manufacturing Processes Examined by Pull-Off Test.

PURPOSE: To investigate the retention loads of differently fabricated secondary telescopic polyetheretherketone (PEEK) crowns on cobalt-chromium primary crowns with different tapers. MATERIALS AND METHODS: Cobalt-chromium primary crowns with 0°, 1°, and 2° tapers were constructed, milled, and sintered. Corresponding secondary crowns were fabricated by milling, pressing from pellets, and pressing from granules. For these nine test groups, the pull-off tests of each crown combination were performed 20 times, and the retention loads were measured (Zwick 1445, 50 mm/min). Data were analyzed using linear regression, covariance analysis, mixed models, Kruskal-Wallis, and Mann-Whitney U-test, together with the Benferroni-Holm correction. RESULTS: The mixed models covariance analysis reinforced stable retention load values (p = 0.162) for each single test sequence. There was no interaction between the groups and the separation cycles (p = 0.179). Milled secondary crowns with 0° showed the lowest mean retention load values compared to all tested groups (p = 0.003) followed by those pressed form pellets with 1°. Regarding the different tapers, no effect of manufacturing method on the results was observed within 1° and 2° groups (p = 0.540; p = 0.052); however, among the 0° groups, the milled ones showed significantly the lowest retention load values (p = 0.002). Among the manufacturing methods, both pressed groups showed no impact of taper on the retention load values (p > 0.324 and p > 0.123, respectively), whereas among the milled secondary crowns, the 0° taper showed significantly lower retention load values than the 1° and 2° taper (p < 0.002). CONCLUSION: Based on these results, telescopic crowns made of PEEK seem to show stable retention load values for each test sequence; however, data with thermo-mechanical aging are still required. In addition, further developments in CAD/CAM manufacturing of PEEK materials for telescopic crowns are warranted, especially for 0°.

Blood Draw Barriers for Treatment with Clozapine and Development of a Point-of-Care Monitoring Device.

BACKGROUND: While clozapine (CLZ) is the most effective antipsychotic drug for schizophrenia treatment, it remains underused. In order to understand the barriers of frequent blood draws for white blood cell counts (WBCs) and clozapine levels, we developed a psychiatrist survey and began an integrative approach of designing a point-of-care device that could eventually have real-time monitoring with immediate results. METHODS: We ascertained barriers related to CLZ management and the acceptance of possible solutions by sending an anonymous survey to physicians in psychiatric practice (n=860). In parallel, we tested CLZ sensing using a prototype point-of-care monitoring device. RESULTS: 255 responses were included in the survey results. The two barriers receiving mean scores with the highest agreement as being a significant barrier were patient nonadherence to blood work and blood work's burden on the patient (out of 28). Among nine solutions, the ability to obtain lab results in the physician's office or pharmacy was top ranked (mean±sd Likert scale [4.0±1.0]). Physicians responded that a point-of-care device to measure blood levels and WBCs would improve care and increase CLZ use. Residents ranked point-of-care devices higher than older physicians (4.07±0.87 vs. 3.47±1.08, p<0.0001). Also, the prototype device was able to detect CLZ reliably in 1.6, 8.2, and 16.3 µg/mL buffered solutions. DISCUSSION: Survey results demonstrate physicians' desire for point-of-care monitoring technology, particularly among younger prescribers. Prototype sensor results identify that CLZ can be detected and integrated for future device development. Future development will also include integration of WBCs for a complete detection device.

Retention force of differently fabricated telescopic PEEK crowns with different tapers.

To assess the retention force between primary and secondary PEEK crowns made by different fabrication methods. Primary crowns with different tapers (0°, 1°, and 2°) were fabricated and secondary crowns that were either milled from breCam BioHPP blanks, pressed from pellets (BioHPP Pellet) or granules (BioHPP Granulat) were produced. Each specimen was measured 20 times in a pulloff-test and results were analyzed using 2-/1-way ANOVA and linear regression analyses (p<0.05). Within 0° tapered crowns milled secondary crowns showed lower retention forces compared to pressed pellet crowns. Crowns with a 1° taper, however, showed no impact of the fabrication method on retention force. At a 2° taper, granular pressed crowns displayed lower values than their milled counterparts. Within the milled group, a 0° taper showed lower retention values than the higher tapers, whereas in the pressed groups, no impact of taper angle on retention force was found.

PEEK Primary Crowns with Cobalt-Chromium, Zirconia and Galvanic Secondary Crowns with Different Tapers-A Comparison of Retention Forces.

In prosthetic dentistry, double crown systems have proved their suitability as retainers for removable partial dentures. However, investigations in this context, regarding polyetheretherketone, are scarce. Therefore, the aim of this study was to test the retention force (RF) between polyetheretherketone (PEEK) primary and cobalt-chromium (CoCr), zirconia (ZrO2) and galvanic (GAL) secondary crowns with three different tapers. Primary PEEK-crowns were milled with the tapers 0°, 1°, and 2° (n = 10/taper, respectively). Afterwards, 90 secondary crowns were fabricated: (i) 30 CoCr-crowns milled from Ceramill Sintron (AmannGirrbach, Koblach, Austria) (n = 10/taper), (ii) 30 ZrO2-crowns milled from Ceramill ZI (AmannGirrbach, Koblach, Austria) (n = 10/taper), and (iii) 30 GAL-crowns made using electroforming (n = 10/taper). RF was measured in a pull-off test (20 pull-offs/specimen) and data were analyzed using 2-/1-way Analysis of Variance (ANOVA) followed by the Tukey-Honestly Significant Difference (HSD) post hoc test and linear regression analyses (p < 0.05). The measured mean RF values ranged between 9.6 and 38.2 N. With regard to the 0°, 1°, and 2° tapered crowns, no statistically significant differences between CoCr and ZrO2 were observed (p > 0.141). At 0° taper, no differences in retention forces between GAL, CrCr, and ZrO2 crowns were found (p = 0.075). However, at 1° and 2° taper, lower RF for GAL-crowns were observed (p < 0.009, p < 0.001, respectively). According to this laboratory study, PEEK might be a suitable material for primary crowns, regardless of the taper and the material of secondary crown. Long-term results, however, are still necessary.

Retention Load Values of Telescopic Crowns Made of Y-TZP and CoCr with Y-TZP Secondary Crowns: Impact of Different Taper Angles.

This study aimed to examine and compare the retention load values (RL) of different telescopic crown assemblies (Y-TZP and CoCr primary crowns with electroformed and Y-TZP secondary crowns each) with three different taper angles (0°, 1° and 2°). Thirty Y-TZP primary crowns with electroformed gold copings (Z/G group) and Y-TZP secondary crowns (Z/Z group) and 30 CoCr primary crowns with electroformed gold copings (C/G group) and Y-TZP secondary crowns (C/Z group), each with taper angles of 0°, 1° and 2°, were fabricated, respectively. With the exception of the electroformed gold copings, all specimens were Computer-Aided-Design/Computer-Aided-Manufacturing (CAD/CAM)-milled, then sintered and afterwards manually adapted. In order to stabilize the gold copings, they were fixed in a tertiary structure. The secondary crowns were constructed with a hook, which ensured self-alignment with an upper chain. Afterwards, 20 pull-off test cycles were performed in a universal testing machine under artificial saliva and after weighing the secondary crowns with a 5 kg object for 20 s. Data were analyzed by one-way and two-way Analysis of Variance (ANOVA). C/Z with 1° showed higher (p = 0.009) RL than 0° and 2° tapers. C/G at 1° also showed higher (p = 0.001) RL than at tapers of 0° and 2°. Z/G and C/G at 0° showed lower RL than Z/Z and C/Z (p < 0.001). Primary crowns had no impact on the 0° group. Z/G showed lower RL as compared to C/Z within the 1° group (p = 0.007) and Z/Z in the 2° group (p = 0.006). The primary crown material had no influence on RL. Electroformed copings showed lower RL. Further investigations for 1° as well as for the long-term performance after thermomechanical aging are necessary.

Suitability of Secondary PEEK Telescopic Crowns on Zirconia Primary Crowns: The Influence of Fabrication Method and Taper.

This study investigates the retention load (RL) between ZrO2 primary crowns and secondary polyetheretherketone (PEEK) crowns made by different fabrication methods with three different tapers. Standardized primary ZrO2 crowns were fabricated with three different tapers: 0°, 1°, and 2° (n = 10/group). Ten secondary crowns were fabricated (i) milled from breCam BioHPP blanks (PM); (ii) pressed from industrially fabricated PEEK pellets (PP) (BioHPP Pellet); or (iii) pressed from granular PEEK (PG) (BioHPP Granulat). One calibrated operator adjusted all crowns. In total, the RL of 90 secondary crowns were measured in pull-off tests at 50 mm/min, and each specimen was tested 20 times. Two- and one-way ANOVAs followed by a Scheffé's post-hoc test were used for data analysis (p < 0.05). Within crowns with a 0° taper, the PP group showed significantly higher retention load values compared with the other groups. Among the 1° taper, the PM group presented significantly lower retention loads than the PP group. However, the pressing type had no impact on the results. Within the 2° taper, the fabrication method had no influence on the RL. Within the PM group, the 2° taper showed significantly higher retention load compared with the 1° taper. The taper with 0° was in the same range value as the 1° and 2° tapers. No impact of the taper on the retention value was observed between the PP groups. Within the PG groups, the 0° taper presented significantly lower RL than the 1° taper, whereas the 2° taper showed no differences. The fabrication method of the secondary PEEK crowns and taper angles showed no consistent effect within all tested groups.

Prophylaxis with antipsychotic medication reduces the risk of post-operative delirium in elderly patients: a meta-analysis.

BACKGROUND: Delirium commonly occurs in hospitalized elderly patients, resulting in increased morbidity and mortality. Although evidence for treatment of delirium exists, evidence supporting pharmacologic prevention of delirium in high risk patients is limited. OBJECTIVE: This review examined whether delirium in at-risk patients can be prevented with antipsychotic prophylaxis in the inpatient setting. DATA SOURCES: A systematic literature review of articles from January 1950 to April 2012 was conducted in PubMed, PsychInfo, and Cochrane Controlled Trials and databases. STUDY SELECTION: Five studies (1491 participants) met our inclusion criteria for analysis. Medication administered included haloperidol (three studies), risperidone (one study), and olanzapine (1 study). All five studies examined older post-surgical patients, spanning five different countries. DATA EXTRACTION: Only RCTs of antipsychotic medication used to prevent delirium were included. Key words used in the search were: "delirium," "encephalopathy," "ICU psychosis," "prevention," and "prophylaxis." Studies had to include a validated method of diagnosing delirium. Data analysis was performed using the Metan command in Stata (Stata Corp LP, College Station, TX). RESULTS: The pooled relative risk of the five studies resulted in a 50% reduction in the relative risk of delirium among those receiving antipsychotic medication compared with placebo (RR(95% CI): 0.51 (0.33-0.79; heterogeneity, p < 0.01, random effects model). Examination of the funnel plot did not indicate publication bias. CONCLUSIONS: Although few studies have examined prophylactic use of antipsychotics, this analysis suggests that perioperative use of prophylactic antipsychotics may effectively reduce the overall risk of postoperative delirium in elderly patients.