Correlation of mineral density and elastic modulus of dog dentin using µ-CT and nanoindentation.

This study sought to 1) investigate the spatial distribution of mineral density of dog dentin using µ-CT and 2) characterize the relationship between the elastic modulus and mineral density of dog dentin using nanoindentation and µ-CT. Maxillary canine teeth of 10 mature dogs were scanned with a µ-CT then sectioned in the transverse and vertical planes and tested using nanoindentation. Spatial distribution of mineral density and elastic modulus was quantified. Results demonstrated significant spatial variation in mineral density and elastic modulus. Mineral density and elastic modulus generally increased from the dentin-pulp interface to the dentino-enamel junction and from the crown base to the crown tip. Significant site dependent correlations between mineral density and elastic modulus were determined (0.021 > R2 > 0.408). The results of this study suggest that while mineral density is a mediator of elastic modulus, other mediators such as collagen content may contribute to the mechanical behavior of dog dentin.

Structure-function relationships in dog dentin.

Investigations into teeth mechanical properties provide insight into physiological functions and pathological changes. This study sought to 1) quantify the spatial distribution of elastic modulus, hardness and the microstructural features of dog dentin and to 2) investigate quantitative relationships between the mechanical properties and the complex microstructure of dog dentin. Maxillary canine teeth of 10 mature dogs were sectioned in the transverse and vertical planes, then tested using nanoindentation and scanning electron microscopy (SEM). Microstructural features (dentin area fraction and dentinal tubule density) and mechanical properties (elastic modulus and hardness) were quantified. Results demonstrated significant anisotropy and spatial variation in elastic modulus, hardness, dentin area fraction and tubule density. These spatial variations adhered to a consistent distribution pattern; hardness, elastic modulus and dentin area fraction generally decreased from superficial to deep dentin and from crown tip to base; tubule density generally increased from superficial to deep dentin. Poor to moderate correlations between microstructural features and mechanical properties (R2 = 0.032-0.466) were determined. The results of this study suggest that the other constituents may contribute to the mechanical behavior of mammalian dentin. Our results also present several remaining opportunities for further investigation into the roles of organic components (e.g., collagen) and mineral content on dentin mechanical behavior.