Adipose- and bone marrow-derived mesenchymal stem cells display different osteogenic differentiation patterns in 3D bioactive glass-based scaffolds.

Mesenchymal stem cells can be isolated from a variety of different sources, each having their own peculiar merits and drawbacks. Although a number of studies have been conducted comparing these stem cells for their osteo-differentiation ability, these are mostly done in culture plastics. We have selected stem cells from either adipose tissue (ADSCs) or bone marrow (BMSCs) and studied their differentiation ability in highly porous three-dimensional (3D) 45S5 Bioglass®-based scaffolds. Equal numbers of cells were seeded onto 5 × 5 × 4 mm3 scaffolds and cultured in vitro, with or without osteo-induction medium. After 2 and 4 weeks, the cell-scaffold constructs were analysed for cell number, cell spreading, viability, alkaline phosphatase activity and osteogenic gene expression. The scaffolds with ADSCs displayed osteo-differentiation even without osteo-induction medium; however, with osteo-induction medium osteogenic differentiation was further increased. In contrast, the scaffolds with BMSCs showed no osteo-differentiation without osteo-induction medium; after application of osteo-induction medium, osteo-differentiation was confirmed, although lower than in scaffolds with ADSCs. In general, stem cells in 3D bioactive glass scaffolds differentiated better than cells in culture plastics with respect to their ALP content and osteogenic gene expression. In summary, 45S5 Bioglass-based scaffolds seeded with ADSCs are well-suited for possible bone tissue-engineering applications. Induction of osteogenic differentiation appears unnecessary prior to implantation in this specific setting. Copyright © 2013 John Wiley & Sons, Ltd.

Osteoinduction and survival of osteoblasts and bone-marrow stromal cells in 3D biphasic calcium phosphate scaffolds under static and dynamic culture conditions.

In many tissue engineering approaches, the basic difference between in vitro and in vivo conditions for cells within three-dimensional (3D) constructs is the nutrition flow dynamics. To achieve comparable results in vitro, bioreactors are advised for improved cell survival, as they are able to provide a controlled flow through the scaffold. We hypothesize that a bioreactor would enhance long-term differentiation conditions of osteogenic cells in 3D scaffolds. To achieve this either primary rat osteoblasts or bone marrow stromal cells (BMSC) were implanted on uniform-sized biphasic calcium phosphate (BCP) scaffolds produced by a 3D printing method. Three types of culture conditions were applied: static culture without osteoinduction (Group A); static culture with osteoinduction (Group B); dynamic culture with osteoinduction (Group C). After 3 and 6 weeks, the scaffolds were analysed by alkaline phosphatase (ALP), dsDNA amount, SEM, fluorescent labelled live-dead assay, and real-time RT-PCR in addition to weekly alamarBlue assays. With osteoinduction, increased ALP values and calcium deposition are observed; however, under static conditions, a significant decrease in the cell number on the biomaterial is observed. Interestingly, the bioreactor system not only reversed the decreased cell numbers but also increased their differentiation potential. We conclude from this study that a continuous flow bioreactor not only preserves the number of osteogenic cells but also keeps their differentiation ability in balance providing a suitable cell-seeded scaffold product for applications in regenerative medicine.