ABSTRACT
The electrospinning technology has set off a tide and given rise to the attention of a widespread range of research territories, benefiting from the enhancement of nanofibers which made a spurt of progress. Nanofibers, continuously produced via electrospinning technology, have greater specific surface area and higher porosity and play a non-substitutable key role in many fields. Combined with the degradability and compatibility of the natural structure characteristics of polysaccharides, electrospun polysaccharide nanofiber membranes gradually infiltrate into the life field to help filter air contamination particles and water pollutants, treat wounds, keep food fresh, monitor electronic equipment, etc., thus improving the life quality. Compared with the evaluation of polysaccharide-based nanofiber membranes in a specific field, this paper comprehensively summarized the existing electrospinning technology and focused on the latest research progress about the application of polysaccharide-based nanofiber in different fields, represented by starch, chitosan, and cellulose. Finally, the benefits and defects of electrospun are discussed in brief, and the prospects for broadening the application of polysaccharide nanofiber membranes are presented for the glorious expectation dedicated to the progress of the eras.
Subject(s)
Chitosan , Nanofibers , Nanofibers/chemistry , Tissue Scaffolds/chemistry , Polysaccharides/chemistry , StarchABSTRACT
Developing fluorine-free superhydrophobic and biodegradable materials for oil/water separation has already become an irresistible trend. In this paper, we designed two biopolymer oil/water separation routes based on cellulose stearoyl ester (CSE), which was obtained via the acylation reaction between dissolving pulp and stearoyl chloride homogeneously. The CSE showed a superhydrophobic property, which could selectively adsorb oil from the oil/water mixture. Additionally, the CSE was emulsified with an oxidized starch (OS) solution, and the resulting latex was used to impregnate commercial, filter base paper, finally obtaining a hydrophobic and oleophilic membrane. The SEM revealed the membrane had hierarchical micro/nanostructures, while the water contact angle indicated the low surface energy of the membrane, all of which were attributed to the CSE. The membrane had high strength and long durability due to the addition of OS/CSE, and the separation efficiency was more than 99% even after ten repeated uses.
ABSTRACT
We prepared super-hydrophobic nanocellulose films using a non-toxic octadecylamine/polydopamine system. Octadecylamine, a low surface energy material, was used to provide hydrophobic alkyl long chains. Polydopamine was produced by dopamine under alkaline conditions, creating an adhesive substance, which reinforced the hydrophobic long chains and increased the surface roughness of nanocellulose. The effects of reagent concentration, reaction temperature, and reaction time on hydrophobicity were then investigated. The results showed that with a 1:1 mass ratio of nanocellulose to octadecylamine, and reacting at 60 °C for 4 h, the contact angle of the obtained composite membrane reached 168.2°. Scanning electron microscope images revealed that the modified nanocellulose had a smaller particle size and more uniform distribution, which effectively improved the hydrophobicity of the nanocellulose. Thus, the green preparation of superhydrophobic films with high-temperature resistance and wear resistance was realized, which contributed to the high-value utilization of nanocellulose.