1.
Small ; : e2400915, 2024 Apr 10.
Article in English | MEDLINE | ID: mdl-38597683

ABSTRACT

Hole transporting layers (HTLs), strategically positioned between electrode and light absorber, play a pivotal role in shaping charge extraction and transport in organic solar cells (OSCs). However, the commonly used poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) HTL, with its hygroscopic and acidic nature, undermines the operational durability of OSC devices. Herein, an environmentally friendly approach is developed utilizing nickel acetate tetrahydrate (NiAc·4H2O) and [2-(9H-carbazol-9-yl)ethyl] phosphonic acid (2PACz) as the NiAc·4H2O/2PACz HTL, aiming at overcoming the limitations posed by the conventional PEDOT:PSS one. Encouragingly, a remarkable power conversion efficiency (PCE) of 19.12% is obtained for the OSCs employing NiAc·4H2O/2PACz as the HTL, surpassing that of devices with the PEDOT:PSS HTL (17.59%), which is ranked among the highest ones of OSCs. This improvement is attributed to the appropriate work function, enhanced hole mobility, facilitated exciton dissociation efficiency, and lower recombination loss of NiAc·4H2O/2PACz-based devices. Furthermore, the NiAc·4H2O/2PACz-based OSCs exhibit superior operational stability compared to their PEDOT:PSS-based counterparts. Of significant note, the NiAc·4H2O/2PACz HTL demonstrates a broad generality, boosting the PCE of the PM6:PY-IT and PM6:Y6-based OSCs from 16.47% and 16.79% (with PEDOT:PSS-based analogs as HTLs) to 17.36% and 17.57%, respectively. These findings underscore the substantial potential of the NiAc·4H2O/2PACz HTL in advancing OSCs, offering improved performance and stability, thereby opening avenue for highly efficient and reliable solar energy harvesting technologies.

2.
Adv Mater ; 36(2): e2305238, 2024 Jan.
Article in English | MEDLINE | ID: mdl-37665975

ABSTRACT

The limited conductivity of existing transparent conducting oxide (TCO) greatly restricts the further performance improvement of perovskite solar cells (PSCs), especially for large-area devices. Herein, buried-metal-grid tin-doped indium oxide (BMG ITO) electrodes are developed to minimize the power loss caused by the undesirable high sheet resistance of TCOs. By burying 140-nm-thick metal grids into ITO using a photolithography technique, the sheet resistance of ITO is reduced from 15.0 to 2.7 Ω sq-1 . The metal step of BMG over ITO has a huge impact on the charge carrier transport in PSCs. The PSCs using BMG ITO with a low metal step deliver power conversion efficiencies (PCEs) significantly better than that of their counterparts with higher metal steps. Moreover, compared with the pristine ITO-based PSCs, the BMG ITO-based PSCs show a smaller PCE decrease when scaling up the active area of devices. The parallel-connected large-area PSCs with an active area of 102.8 mm2 reach a PCE of 22.5%. The BMG ITO electrodes are also compatible with the fabrication of inverted-structure PSCs and organic solar cells. The work demonstrates the great efficacy of improving the conductivity of TCO by BMG and opens up a promising avenue for constructing highly efficient large-area PSCs.

3.
Adv Mater ; 35(49): e2308334, 2023 Dec.
Article in English | MEDLINE | ID: mdl-37822055

ABSTRACT

Laboratory-scale all-polymer solar cells (all-PSCs) have exhibited remarkable power conversion efficiencies (PCEs) exceeding 19%. However, the utilization of hazardous solvents and nonvolatile liquid additives poses challenges for eco-friendly commercialization, resulting in the trade-off between device efficiency and operation stability. Herein, an innovative approach based on isomerized solid additive engineering is proposed, employing volatile dithienothiophene (DTT) isomers to modulate intermolecular interactions and facilitate molecular stacking within the photoactive layers. Through elucidating the underlying principles of the DTT-induced polymer assembly on molecular level, a PCE of 18.72% is achieved for devices processed with environmentally benign solvents, ranking it among the highest record values for eco-friendly all-PSCs. Significantly, such superiorities of the DTT-isomerized strategy afford excellent compatibility with large-area blade-coating techniques, offering a promising pathway for industrial-scale manufacturing of all-PSCs. Moreover, these devices demonstrate enhanced thermal stability with a promising extrapolated T80 lifetime of 14 000 h, further bolstering their potential for sustainable technological advancement.

4.
Nat Commun ; 14(1): 967, 2023 Feb 21.
Article in English | MEDLINE | ID: mdl-36810743

ABSTRACT

Degradation of the kinetically trapped bulk heterojunction film morphology in organic solar cells (OSCs) remains a grand challenge for their practical application. Herein, we demonstrate highly thermally stable OSCs using multicomponent photoactive layer synthesized via a facile one-pot polymerization, which show the advantages of low synthetic cost and simplified device fabrication. The OSCs based on multicomponent photoactive layer deliver a high power conversion efficiency of 11.8% and exhibit excellent device stability for over 1000 h (>80% of their initial efficiency retention), realizing a balance between device efficiency and operational lifetime for OSCs. In-depth opto-electrical and morphological properties characterizations revealed that the dominant PM6-b-L15 block polymers with backbone entanglement and the small fraction of PM6 and L15 polymers synergistically contribute to the frozen fine-tuned film morphology and maintain well-balanced charge transport under long-time operation. These findings pave the way towards the development of low-cost and long-term stable OSCs.

5.
Neurobiol Dis ; 174: 105872, 2022 Nov.
Article in English | MEDLINE | ID: mdl-36152944

ABSTRACT

Drug resistance is a major challenge in the treatment of epilepsy. Drug-resistant epilepsy (DRE) accounts for 30% of all cases of epilepsy and is a matter of great concern because of its uncontrollability and the high burden, mortality rate, and degree of damage. At present, considerable research has focused on the development of predictors to aid in the early identification of DRE in an effort to promote prompt initiation of individualized treatment. While multiple predictors and risk factors have been identified, there are currently no standard predictors that can be used to guide the clinical management of DRE. In this review, we discuss several potential predictors of DRE and related factors that may become predictors in the future and perform evidence rating analysis to identify reliable potential predictors.


Subject(s)
Drug Resistant Epilepsy , Epilepsy , Humans , Drug Resistant Epilepsy/diagnosis , Drug Resistant Epilepsy/etiology , Epilepsy/diagnosis , Epilepsy/drug therapy , Epilepsy/complications , Risk Factors , Drug Resistance , Biomarkers
6.
ACS Nano ; 16(8): 11902-11911, 2022 Aug 23.
Article in English | MEDLINE | ID: mdl-35866886

ABSTRACT

Charge carrier nonradiative recombination (NRR) caused by interface defects and nonoptimal energy level alignment is the primary factor restricting the performance improvement of perovskite solar cells (PSCs). Interfacial modification is a vital strategy to restrain NRR and enable high-performance PSCs. We report here two interfacial materials, PhI-TPA and BTZI-TPA, consisting of phthalimide and a 2,1,3-benzothiadiazole-5,6-dicarboxylicimide core, respectively. The difunctionalized BTZI-TPA with imide and thiadiazole shows higher hole mobility, better aligned energy levels, and stronger interaction with uncoordinated Pb2+ on the perovskite surface, suppressing NRR and carrier accumulation at the interface of perovskite/spiro-OMeTAD and yielding enhanced open-circuit voltage and fill factor. Consequently, the PSC based on BTZI-TPA delivers a high efficiency of 24.06% with an excellent fill factor of 83.10%, superior to that (21.47%) of the reference cell without an interfacial layer, and 21.45% efficiency for the device with a scaled-up area (1.00 cm2). These results underscore the potential of imide and thiadiazole groups in developing interfacial layers with strong passivation capability, effective charge transport property, and fine-tuned energetics for stable and efficient PSCs.

7.
Nature ; 599(7883): 67-73, 2021 11.
Article in English | MEDLINE | ID: mdl-34732866

ABSTRACT

Chemical doping is a key process for investigating charge transport in organic semiconductors and improving certain (opto)electronic devices1-9. N(electron)-doping is fundamentally more challenging than p(hole)-doping and typically achieves a very low doping efficiency (η) of less than 10%1,10. An efficient molecular n-dopant should simultaneously exhibit a high reducing power and air stability for broad applicability1,5,6,9,11, which is very challenging. Here we show a general concept of catalysed n-doping of organic semiconductors using air-stable precursor-type molecular dopants. Incorporation of a transition metal (for example, Pt, Au, Pd) as vapour-deposited nanoparticles or solution-processable organometallic complexes (for example, Pd2(dba)3) catalyses the reaction, as assessed by experimental and theoretical evidence, enabling greatly increased η in a much shorter doping time and high electrical conductivities (above 100 S cm-1; ref. 12). This methodology has technological implications for realizing improved semiconductor devices and offers a broad exploration space of ternary systems comprising catalysts, molecular dopants and semiconductors, thus opening new opportunities in n-doping research and applications12, 13.

8.
Acc Chem Res ; 54(20): 3804-3817, 2021 Oct 19.
Article in English | MEDLINE | ID: mdl-34617720

ABSTRACT

ConspectusIn the last three decades, p-type (hole-transporting) organic and polymeric semiconductors have achieved great success in terms of materials diversity and device performance, while the development of n-type (electron-transporting) analogues greatly lags behind, which is limited by the scarcity of highly electron-deficient building blocks with compact geometry and good solubility. However, such n-type semiconductors are essential due to the existence of the p-n junction and a complementary metal oxide semiconductor (CMOS)-like circuit in organic electronic devices. Among various electron-deficient building blocks, imide-functionalized arenes, such as naphthalene diimide (NDI) and perylene diimide (PDI), have been proven to be the most promising ones for developing n-type organic and polymeric semiconductors. Nevertheless, phenyl-based NDI and PDI lead to sizable steric hindrance with neighboring (hetero)arenes and a high degree of backbone distortion in the resultant semiconductors, which greatly limits their microstructural ordering and charge transport. To attenuate the steric hindrance associated with NDI and PDI, a novel imide-functionalized heteroarene, bithiophene imide (BTI), was designed; however, the BTI-based semiconductors suffer from high-lying frontier molecular orbital (FMO) energy levels as a result of their electron-rich thiophene framework and monoimide group, which is detrimental to n-type performance.In this Account, we review a series of BTI derivatives developed via various strategies, including ring fusion, thiazole substitution, fluorination, cyanation, and chalcogen substitution, and elaborate the synthesis routes designed to overcome the synthesis challenges due to their high electron deficiency. After structural optimization, these BTI derivatives can not only retain the advantages of good solubility, a planar backbone, and small steric hindrance inherited from BTI but also have greatly suppressed FMO levels. These novel building blocks enable the construction of a great number of n-type organic and polymeric semiconductors, particularly acceptor-acceptor (or all-acceptor)-type polymers, with remarkable performance in various devices, including electron mobility (µe) of 3.71 cm2 V-1 s-1 in organic thin-film transistors (OTFTs), a power conversion efficiency (PCE) of 15.2% in all-polymer solar cells (all-PSCs), a PCE of 20.8% in inverted perovskite solar cells (PVSCs), electrical conductivity (σ) of 0.34 S cm-1 and a power factor (PF) of 1.52 µW m-1 K-2 in self-doped diradicals, and σ of 23.3 S cm-1 and a PF of ∼10 µW m-1 K-2 in molecularly n-doped polymers, all of which are among the best values in each type of device. The structure-property-device performance correlations of these n-type semiconductors are elucidated. The design strategy and synthesis of these novel BTI derivatives provide important information for developing highly electron-deficient building blocks with optimized physicochemical properties. Finally, we offer our insights into the further development of BTI derivatives and semiconductors built from them.

9.
Adv Mater ; 33(37): e2102635, 2021 Sep.
Article in English | MEDLINE | ID: mdl-34338383

ABSTRACT

Narrow-bandgap n-type polymers with high electron mobility are urgently demanded for the development of all-polymer solar cells (all-PSCs). Here, two regioregular narrow-bandgap polymer acceptors, L15 and MBTI, with two electron-deficient segments are synthesized by copolymerizing two dibrominated fused-ring electron acceptors (FREA) with distannylated aromatic imide, respectively. Taking full advantage of the FREA and the imide, both polymer acceptors show narrow bandgap and high electron mobility. Benefiting from the more extended absorption, better backbone ordering, and higher electron mobility than those of its regiorandom analog, the L15-based all-PSC yields a high power conversion efficiency (PCE) of 15.2% when blended with the polymer donor PM6. More importantly, MBTI incorporating a benzothiophene-core FREA segment shows relatively higher frontier molecular orbital levels than L15, forming a cascade-like energy level alignment with L15 and PM6. Based on this, ternary all-PSCs are designed where MBTI is introduced as a guest into the PM6:L15 host system. Thanks to further optimal blend morphology and more balanced charge transport, the PCE is improved up to 16.2%, which is among the highest values for all-PSCs. The results demonstrate that combining an FREA and an aromatic imide to construct regioregular narrow-bandgap polymer acceptors provides an effective approach to fabricate highly efficient all-PSCs.

10.
ACS Appl Mater Interfaces ; 13(14): 16744-16753, 2021 Apr 14.
Article in English | MEDLINE | ID: mdl-33818080

ABSTRACT

Conductive polyelectrolytes such as P3CT-Na have been widely used as efficient hole-transporting layers (HTLs) in inverted perovskite solar cells (PSCs) due to their high hole mobility. However, the acid-base neutralization reaction is indispensable for preparing such polyelectrolytes and the varied content of cations usually leads to poor reproducibility of the device performance in PSCs. In this work, a commercially available polymer poly[3-(4-carboxybutyl)thiophene-2,5-diyl] (P3CT) was directly applied as an HTL in PSCs for the first time. Encouragingly, it was found that due to the dual functionality of carboxyl groups on side chains, a thin layer of P3CT can not only strongly anchor on ITO electrode and optimize its work function but also show an effective passivation effect toward perovskite active layer. Benefiting from such dual functionality, a uniform perovskite film with better quality was obtained on P3CT. As a result, the P3CT-based PSCs show much lower nonradiative recombination and achieve a champion power conversion efficiency (PCE) of 21.33% with a high fill factor (FF) of 83.6%. Impressively, as the device area is increased to 0.80 cm2, a PCE of 19.65% can still be obtained for the PSCs based on P3CT HTL. Our work provides important strategy for developing HTLs for high-performance PSCs.

11.
ACS Omega ; 6(11): 7896-7909, 2021 Mar 23.
Article in English | MEDLINE | ID: mdl-33778301

ABSTRACT

The purpose of this study was to synthesize a magnetic material that could be easily separated by a magnetic field and combined the catalytic function of an acid/base ionic liquid with silicon for biodiesel preparation. A kind of magnetic catalyst-immobilized ionic liquid was synthesized by a three-step method. The synthesis conditions in each step were optimized by single-factor analysis. Under the optimum conditions, 206.83 mg of ionic liquid (>43.63%) was immobilized on SiO2 (per gram). Heating under reflux was applied to extract Schisandra chinensis seed oil with an average yield of 10.9%. According to the biodiesel yields, Fe3O4@SiO2@[C4mim]HSO4 was the most efficient catalyst in the methyl esterification reaction. Under the optimum reaction conditions, seed oil (10.0 g) was mixed with methanol (70 mL) under continuous mechanical stirring for 3 h, and the yield of biodiesel was 0.557 g/g (the catalyst efficiency was about 89.2%). Also, the thermal value was increased from 32.14 kJ/g (seed oil) to 38.28 kJ/g (biodiesel). The catalytic efficiency of Fe3O4@SiO2@[C4mim]HSO4 was 87.6% of the first being used after four reuse cycles, and 71.4% of the first being used after six reuse cycles in the methylation reaction. The yields and physical and chemical properties of biodiesel were determined.

12.
Adv Mater ; 32(48): e2005942, 2020 Dec.
Article in English | MEDLINE | ID: mdl-33118246

ABSTRACT

Recent advances in the development of polymerized A-D-A-type small-molecule acceptors (SMAs) have promoted the power conversion efficiency (PCE) of all-polymer solar cells (all-PSCs) over 13%. However, the monomer of an SMA typically consists of a mixture of three isomers due to the regio-isomeric brominated end groups (IC-Br(in) and IC-Br(out)). In this work, the two isomeric end groups are successfully separated, the regioisomeric issue is solved, and three polymer acceptors, named PY-IT, PY-OT, and PY-IOT, are developed, where PY-IOT is a random terpolymer with the same ratio of the two acceptors. Interestingly, from PY-OT, PY-IOT to PY-IT, the absorption edge gradually redshifts and electron mobility progressively increases. Theory calculation indicates that the LUMOs are distributed on the entire molecular backbone of PY-IT, contributing to the enhanced electron transport. Consequently, the PM6:PY-IT system achieves an excellent PCE of 15.05%, significantly higher than those for PY-OT (10.04%) and PY-IOT (12.12%). Morphological and device characterization reveals that the highest PCE for the PY-IT-based device is the fruit of enhanced absorption, more balanced charge transport, and favorable morphology. This work demonstrates that the site of polymerization on SMAs strongly affects device performance, offering insights into the development of efficient polymer acceptors for all-PSCs.

13.
Adv Mater ; 32(43): e2004183, 2020 Oct.
Article in English | MEDLINE | ID: mdl-32954584

ABSTRACT

Narrow-bandgap polymer semiconductors are essential for advancing the development of organic solar cells. Here, a new narrow-bandgap polymer acceptor L14, featuring an acceptor-acceptor (A-A) type backbone, is synthesized by copolymerizing a dibrominated fused-ring electron acceptor (FREA) with distannylated bithiophene imide. Combining the advantages of both the FREA and the A-A polymer, L14 not only shows a narrow bandgap and high absorption coefficient, but also low-lying frontier molecular orbital (FMO) levels. Such FMO levels yield improved electron transfer character, but unexpectedly, without sacrificing open-circuit voltage (Voc ), which is attributed to a small nonradiative recombination loss (Eloss,nr ) of 0.22 eV. Benefiting from the improved photocurrent along with the high fill factor and Voc , an excellent efficiency of 14.3% is achieved, which is among the highest values for all-polymer solar cells (all-PSCs). The results demonstrate the superiority of narrow-bandgap A-A type polymers for improving all-PSC performance and pave a way toward developing high-performance polymer acceptors for all-PSCs.

14.
Small ; 16(30): e2001942, 2020 Jul.
Article in English | MEDLINE | ID: mdl-32602255

ABSTRACT

Understanding the conformation effect on molecular packing, miscibility, and photovoltaic performance is important to open a new avenue for small-molecule acceptor (SMA) design. Herein, two novel acceptor-(donor-acceptor1-donor)-acceptor (A-DA1D-A)-type asymmetric SMAs are developed, namely C-shaped BDTP-4F and S-shaped BTDTP-4F. The BDTP-4F-based polymer solar cells (PSCs) with PM6 as donor, yields a power conversion efficiency (PCE) of 15.24%, significantly higher than that of the BTDTP-4F-based device (13.12%). The better PCE for BDTP-4F-based device is mainly attributed to more balanced charge transport, weaker bimolecular recombination, and more favorable morphology. Additionally, two traditional A-D-A-type SMAs (IDTP-4F and IDTTP-4F) are also synthesized to investigate the conformation effect on morphology and device performance. Different from the device result above, here, IDTP-4F with S-shape conformation outperforms than IDTTP-4F with C-shape conformation. Importantly, it is found that for these two different types of SMA, the better performing binary blend has similar morphological characteristics. Specifically, both PM6:BDTP-4F and PM6:IDTP-4F blend exhibit perfect nanofibril network structure with proper domain size, obvious face-on orientation and enhance donor-acceptor interactions, thereby better device performance. This work indicates tuning molecular conformation plays pivotal role in morphology and device effciciency, shining a light on the molecular design of the SMAs.

15.
ACS Appl Mater Interfaces ; 12(23): 25843-25852, 2020 Jun 10.
Article in English | MEDLINE | ID: mdl-32419443

ABSTRACT

Developing scalable and robust processing methods with low material waste remains a challenge for organic solar cells (OSCs) to become a practical renewable energy source. Here, we present a novel low-cost processing approach termed as soft porous blade printing (SPBP), which uses a layer of soft porous material such as filter paper as the printing blade. The inherent porous microstructure of the blade offers high shear rates that facilitate the alignment, crystallization, and orientation of active materials during printing. Moreover, by eliminating the suspended liquid meniscus, SPBP relaxes the stringent requirement of gap control and enables continuous ink delivery for uninterrupted film fabrication with adjustable thickness. Higher photovoltaic performances are achieved in the SPBP-printed OSCs than those of the spin-coated counterparts for two nonfullerene-acceptor active-layer systems (Y6:PM6 and PTQ10:IDIC). Y6:PM6 cells printed by SPBP without any additive exhibit power conversion efficiencies up to 14.75%, which is among the highest reported to date for non-spin-coated OSCs.

16.
J Am Chem Soc ; 142(9): 4329-4340, 2020 Mar 04.
Article in English | MEDLINE | ID: mdl-32048836

ABSTRACT

Unpaired electrons of organic radicals can offer high electrical conductivity without doping, but they typically suffer from low stability. Herein, we report two organic diradicaloids based on quinoidal oligothiophene derivative (QOT), that is, BTICN and QTICN, with high stability and conductivity by employing imide-bridged fused molecular frameworks. The attachment of a strong electron-withdrawing imide group to the tetracyano-capped QOT backbones enables extremely deeply aligned LUMO levels (from -4.58 to -4.69 eV), cross-conjugated diradical characters, and remarkable ambient stabilities of the diradicaloids with half-lives > 60 days, which are among the highest for QOT diradicals and also the widely explored polyaromatic hydrocarbon (PAH)-based diradicals. Specifically, QTICN based on a tetrathiophene imide exhibits a cross-conjugation assisted self-doping in the film state as revealed by XPS and Raman studies. This property in combination with its ordered packing yields a high electrical conductivity of 0.34 S cm-1 for the QTICN films with substantial ambient stability, which is also among the highest values in organic radical-based undoped conductive materials reported to date. When used as an n-type thermoelectric material, QTICN shows a promising power factor of 1.52 uW m-1 K-2. Our results not only provide new insights into the electron conduction mechanism of the self-doped QOT diradicaloids but also demonstrate the great potential of fused quinoidal oligothiophene imides in developing stable diradicals and high-performance doping-free n-type conductive materials.

17.
Dalton Trans ; 49(12): 3723-3734, 2020 Mar 28.
Article in English | MEDLINE | ID: mdl-31720636

ABSTRACT

A g-C3N4/ZnO/cellulose ternary composite (labeled as CNZCel) with an ordered structure and excellent antibacterial properties has been successfully synthesized via a facile method. Its morphology, microstructure and components have been analyzed by using XRD, SEM, TEM and EDS, and the results corroborate the co-existence of three components in the ternary composite. It is revealed that ZnO particles are connected to the layered g-C3N4 and simultaneously attached to the cellulose substrate. This microstructural feature is also borne out by the relativistic density functional study of a finite g-C3N4-ZnO-cellulose cluster. Both experimental and theoretical results unravel that the interfacial bonding interactions in the ternary composite improve electron transfer among components and enable high-efficiency spatial separation of photogenerated electrons and holes. Consequently, good antibacterial performance of the composite has been found in tests. This study provides the prospect of preparing low-cost and environment-friendly food packaging materials, which are also endowed with excellent antibacterial activity.


Subject(s)
Anti-Bacterial Agents/pharmacology , Cellulose/pharmacology , Graphite/pharmacology , Nanocomposites/chemistry , Nitrogen Compounds/pharmacology , Zinc Oxide/pharmacology , Anti-Bacterial Agents/chemical synthesis , Anti-Bacterial Agents/chemistry , Cellulose/chemistry , Density Functional Theory , Escherichia coli/drug effects , Graphite/chemistry , Microbial Sensitivity Tests , Nitrogen Compounds/chemistry , Particle Size , Staphylococcus aureus/drug effects , Surface Properties , Zinc Oxide/chemistry
18.
Macromol Rapid Commun ; 40(23): e1900394, 2019 Dec.
Article in English | MEDLINE | ID: mdl-31702099

ABSTRACT

Diketopyrrolopyrrole (DPP)-based copolymers have received considerable attention as promising semiconducting materials for high-performance organic thin-film transistors (OTFTs). However, these polymers typically exhibit p-type or ambipolar charge-transporting characteristics in OTFTs due to their high-lying highest occupied molecular orbital (HOMO) energy levels. In this work, a new series of DPP-based n-type polymers have been developed by incorporating fused bithiophene imide oligomers (BTIn) into DPP polymers. The resulting copolymers BTIn-DPP show narrow band gaps as low as 1.27 eV and gradually down-shifted frontier molecular orbital energy levels upon the increment of imide group number. Benefiting from the coplanar backbone conformation, well-delocalized π-system, and favorable polymer chain packing, the optimal polymer in the series shows promising n-type charge transport with an electron mobility up to 0.48 cm2 V-1 s-1 in OTFTs, which is among the highest values for the DPP-based n-type polymers reported to date. The results demonstrate that incorporating fused bithiophene imide oligomers into polymers can serve as a promising strategy for constructing high-performance n-type polymeric semiconductors.


Subject(s)
Imides/chemistry , Ketones/chemistry , Polymers/chemical synthesis , Pyrroles/chemistry , Thiophenes/chemistry , Density Functional Theory , Molecular Structure , Polymers/chemistry , Semiconductors , Transistors, Electronic
19.
Adv Sci (Weinh) ; 6(21): 1901773, 2019 Nov 06.
Article in English | MEDLINE | ID: mdl-31728295

ABSTRACT

Significant progress has been made in nonfullerene small molecule acceptors (NF-SMAs) that leads to a consistent increase of power conversion efficiency (PCE) of nonfullerene organic solar cells (NF-OSCs). To achieve better compatibility with high-performance NF-SMAs, the direction of molecular design for donor polymers is toward wide bandgap (WBG), tailored properties, and preferentially ecofriendly processability for device fabrication. Here, a weak acceptor unit, methyl 2,5-dibromo-4-fluorothiophene-3-carboxylate (FE-T), is synthesized and copolymerized with benzo[1,2-b:4,5-b']dithiophene (BDT) to afford a series of nonhalogenated solvent processable WBG polymers P1-P3 with a distinct side chain on FE-T. The incorporation of FE-T leads to polymers with a deep highest occupied molecular orbital (HOMO) level of -5.60-5.70 eV, a complementary absorption to NF-SMAs, and a planar molecular conformation. When combined with the narrow bandgap acceptor ITIC-Th, the solar cell based on P1 with the shortest methyl chain on FE-T achieves a PCE of 11.39% with a large V oc of 1.01 V and a J sc of 17.89 mA cm-2. Moreover, a PCE of 12.11% is attained for ternary cells based on WBG P1, narrow bandgap PTB7-Th, and acceptor IEICO-4F. These results demonstrate that the new FE-T is a highly promising acceptor unit to construct WBG polymers for efficient NF-OSCs.

20.
ACS Appl Mater Interfaces ; 11(39): 35924-35934, 2019 Oct 02.
Article in English | MEDLINE | ID: mdl-31525945

ABSTRACT

Imide functionalization is one of the most effective approaches to develop electron-deficient building blocks for constructing n-type organic semiconductors. Driven by the attractive properties of imide-functionalized dithienylbenzodiimide (TBDI) and the promising device performance of TBDI-based polymers, a novel acceptor with increased electron affinity, fluorinated dithienylbenzodiimide (TFBDI), was designed with the hydrogen replaced by fluorine on the benzene core, and the synthetic challenges associated with this highly electron-deficient fluorinated imide building block are successfully overcome. TFBDI showed suppressed frontier molecular orbital energy levels as compared with TBDI. Copolymerizing this new electron-withdrawing TBDI with various donor co-units afforded a series of n-type polymer semiconductors TFBDI-T, TFBDI-Se, and TFBDI-BSe. All these TFBDI-based polymers exhibited a lower-lying lowest unoccupied molecular orbital (LUMO) energy level than the polymer analogue without fluorine. When applied in organic thin-film transistors, three polymers showed unipolar electron transport with large on-current/off-current ratios (Ion/Ioff) of 105-107. Among them, the selenophene-based polymer TFBDI-Se with the deepest-positioned LUMO and optimal chain stacking exhibited the highest electron mobility of 0.30 cm2 V-1 s-1. This result demonstrates that the new TFBDI is a highly attractive electron-deficient unit for enabling n-type polymer semiconductors, and the fluorination of imide-functionalized arenes offers an effective approach to develop more electron-deficient building blocks in organic electronics.