An investigation of the microstructure and mechanical properties of dental zirconia manufactured by digital light processing 3D printing.

OBJECTIVES: This study was performed to investigate the microstructure and mechanical properties of dental zirconia manufactured by digital light processing (DLP) 3D printing and the clinical application prospects of this material. METHODS: The experiment (DLP) group was zirconia manufactured by DLP 3D printing, and the control (MILL) group was milled zirconia. The density, grain size, and phase composition were measured to study the microstructure. Flexural strength was measured by using three-point bending tests, while Vickers hardness was determined through a Vickers hardness tester. Fracture toughness was tested using the single-edge V-notched beam method. RESULTS: Zirconia density of the DLP group was (6.019 8±0.021 3) g·cm-3, and the average grain size was (0.603 0±0.032 6) µm, but without statistical difference with the corresponding values of the MILL group (P>0.05). Tetragonal phase was found in the X-ray diffraction patterns of the DLP and MILL groups. The flexural strength of the DLP group was (1 012.7±125.5) MPa, and Vickers hardness was (1 238.5±10.8) HV1, which was slightly lower than that of the MILL group (P<0.05). The fracture toughness of the DLP group was (7.22±0.81) MPa·m1/2, which was not statistically different from that of the MILL group (P>0.05). CONCLUSIONS: Zirconia manufactured by DLP 3D printing had microstructure and mechanical properties similar to those of the milled zirconia. Only the flexural strength and the Vickers hardness of the experimental zirconia were slightly lower than those of the milled zirconia. Therefore, DLP-manufactured zirconia has a promising future for clinical use.

[Research progress in the relationship between Veillonella and oral diseases].

Veillonella species, known as the early colonizer of oral biofilm, are prevalent in oral microbiota. Seven Veillonella species have been isolated from oral cavity. Their distribution varies not only with different people but also with different sites in the oral cavity. Oral Veillonella are associated with oral diseases. They contribute to the adhesion of Streptococcus mutans and consume the lactate generated by streptococci. Veillonella species play an important role in the occurrence and development of periodontal diseases by providing adhesion sites for Porphyromonas gingivalis and boosting immune responses. The production of lipopolysaccharide and H2S is related to other oral diseases, such as pulpitis, periapical periodontitis, and halitosis. Several studies have been conducted on the relationship between Veillonella and oral diseases and the interaction between Veillonella and other pathological microorganisms, but limited knowledge is available at the molecular level. This article reviews the research progress in the relationship between Veillonella and oral infectious diseases, such as dental caries and periodontal diseases.