ABSTRACT
Articular cartilages exhibit load-bearing capacity and durability due to their inhomogeneous structure. Inspired by this unique structure, a tough and inhomogeneous salt-hydrogel was developed by trapping sodium acetate (NaAc) crystals in polyacrylamide (PAM) polymer networks and then partially redissolving the NaAc crystals. The compressive and tensile stresses of the salt-hydrogel increase significantly by more than 20 times when oversaturated Ac- and Na+ are introduced into the gel network. Such an enhancement in mechanical strength is primarily attributed to the formation of NaAc crystals within the gel network. Further investigations reveal that the mechanical strength of the salt-hydrogel is temperature-dependent as the NaAc crystals gradually redissolve in the gel network with increasing temperature. Furthermore, redissolving NaAc crystals in an aqueous solution can yield an inhomogeneous salt-hydrogel. The topmost soft surface of the salt-hydrogel offers hydration lubrication, while the inhomogeneous network confers load-bearing capacity and durability. Compared to regular hydrogels, the inhomogeneous salt-hydrogel surface can realize drag reduction and remain smooth without damage after the friction tests. Moreover, a salt-hydrogel coating is also fabricated to visually demonstrate its drag-reducing property. In addition, this salt-hydrogel possesses conductivity and can be utilized in the development of inhomogeneous salt-hydrogel fibers (diameter = 438 ± 7 µm) for strain detection. The produced salt-hydrogel fiber exhibits excellent durability and reproducibility as a strain sensor, capable of detecting both small strains (e.g., 1%) and large strains (e.g., 40%). This work provides fundamental insights into developing hydrogels with an inhomogeneous network and explores their potential applications (e.g., hydrated drag-reducing, strain sensing).