ABSTRACT
A previously unreported polymorph of 5,11-bis(triisopropylsilylethynyl)anthradithiophene (TIPS ADT), Form II, crystallizes from melt-processed TIPS ADT films blended with 16 ± 1 wt % medium density polyethylene (PE). TIPS ADT/PE blends that initially are crystallized from the melt produce twisted TIPS ADT crystals of a metastable polymorph (Form IV, space group P1Ì ) with a brickwork packing motif distinct from the slipstack packing by solution-processed TIPS ADT crystals (Form I, space group P21/c) at room temperature. When these films were cooled to room temperature and subsequently annealed at 100 °C, near a PE melting temperature of 110 °C, Form II crystals nucleated and grew while consuming Form IV. The growth rate and orientations of Form II crystals were predetermined by the twisting pitch and growth direction of the original banded spherulites in the melt-processed films of the blends. Notably, the Form IV â II transition was not observed during thermal annealing of neat TIPS ADT films without PE. The presence of the mobile PE phase during thermal annealing of TIPS ADT/PE blend films increases the diffusion rate of TIPS ADT molecules, and the rate of nucleation of Form II. Form IV crystals are more conductive but less emissive compared to Form II crystals.
ABSTRACT
The performance of crystalline organic semiconductors depends on the solid-state structure, especially the orientation of the conjugated components with respect to device platforms. Often, crystals can be engineered by modifying chromophore substituents through synthesis. Meanwhile, dissymetry is necessary for high-tech applications like chiral sensing, optical telecommunications, and data storage. The synthesis of dissymmetric molecules is a labor-intensive exercise that might be undermined because common processing methods offer little control over orientation. Crystal twisting has emerged as a generalizable method for processing organic semiconductors and offers unique advantages, such as patterning of physical and chemical properties and chirality that arises from mesoscale twisting. The precession of crystal orientations can enrich performance because achiral molecules in achiral space groups suddenly become candidates for the aforementioned technologies that require dissymetry.