J Nanosci Nanotechnol ; 6(8): 2484-8, 2006 Aug.
Article in English | MEDLINE | ID: mdl-17037860

ABSTRACT

Delamination/exfoliation process of the Mg-vermiculite (Letovice, Czech Republic), particles with size less than 5 microm, was studied after potassium persulfate treatment and compared with known method utilized hydrogen peroxide treatment. X-ray powder diffraction (XRPD) patterns showed that treatment of Mg-vermiculite with different molar concentration of potassium persulfate: c = 0.02, 0.04, and 0.08 mol x dm(-3) at the temperature 60 degrees C for 2 hr caused reduction of relative intensity (I(rel.)) of the basal 001 diffraction to the 15%, 9%, and 4%, respectively, compared to intensity of 001 diffraction of untreated Mg-vermiculite (I(rel.) = 100%). On the other hand I(rel.) of the 001 diffraction of Mg-vermiculite after treatment with 30% and 50% (c = 9.8 and 17.4 mol x dm(-3)) hydrogen peroxide at the 60 degrees C for 2 hr decreased only to I(rel.) = 36% and 32%, respectively. Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM) verified effect of potassium persulfate treatment on structure degradation which is connected with higher degree of delamination/exfoliation of the particles and their cracking into nano-sized particles.


Subject(s)
Aluminum Silicates/chemistry , Magnesium/chemistry , Microscopy, Atomic Force/methods , Nanoparticles/chemistry , Nanotechnology/methods , Potassium Compounds/pharmacology , Sulfates/pharmacology , Hydrogen Peroxide/chemistry , Microscopy, Electron, Scanning , Nanostructures/chemistry , Temperature , Time Factors , X-Ray Diffraction
2.
J Nanosci Nanotechnol ; 6(3): 726-30, 2006 Mar.
Article in English | MEDLINE | ID: mdl-16573128

ABSTRACT

Powdered natural Mg-vermiculite (Letovice, Czech Republic), with the formula (Mg0.35K0.02Ca0.01) (Mg2.39Fe0.51(3+)Fe0.02(2+)Al0.08) (Si2.64Al1.33Ti0.03) O10(OH)2 x 4.97H2O and particle size < 5 microm, was used for the investigation of exfoliation after hydrogen peroxide and/or microwave treatment (600 W). A sample heated in the microwave oven for 40 min exhibits a 11% mass loss and reduction of the 001 peak intensity in the X-ray diffraction pattern. The basal 001 peak intensity of untreated Mg-vermiculite sample (/001 = 100%) drops to 35% in the microwave treated sample. Only the sample treated for 5 h at 80 degrees C fully rehydrated after 120 min at room temperature. A more pronounced reduction of the 001 peak intensity (to 8%) was observed after hydrogen peroxide treatment of the sample at 25 degrees C. The combination of a five-hour hydrogen peroxide treatment at 80 degrees C and subsequent microwave heating leads to an effective extinction of the 001 diffraction in the XRD pattern. The 001 diffraction profile becomes very diffuse with peak intensity less than 1%. The degree of reduction of the 001 diffraction intensity also depends on the time and temperature of hydrogen peroxide treatment and on the peroxide concentration. An even more pronounced reduction of the peak intensity is caused by exfoliation of particles to nano-domains coupled with a randomization of the c-axes.


Subject(s)
Aluminum Silicates/chemistry , Crystallization/methods , Hot Temperature , Hydrogen Peroxide/chemistry , Magnesium/chemistry , Nanostructures/chemistry , Nanostructures/ultrastructure , Nanotechnology/methods , Aluminum Silicates/analysis , Molecular Conformation , Particle Size