Graft Polymerization of Acrylamide in an Aqueous Dispersion of Collagen in the Presence of Tributylborane.

Graft copolymers of collagen and polyacrylamide (PAA) were synthesized in a suspension of acetic acid dispersion of fish collagen and acrylamide (AA) in the presence of tributylborane (TBB). The characteristics of the copolymers were determined using infrared spectroscopy and gel permeation chromatography (GPC). Differences in synthesis temperature between 25 and 60 °C had no significant effect on either proportion of graft polyacrylamide generated or its molecular weight. However, photomicrographs taken with the aid of a scanning electron microscope showed a breakdown of the fibrillar structure of the collagen within the copolymer at synthesis temperatures greater than 25 °C. The mechanical properties of the films and the cytotoxicity of the obtained copolymer samples were studied. The sample of a hybrid copolymer of collagen and PAA obtained at 60 °C has stronger mechanical properties compared to other tested samples. Its low cytotoxicity, when the monomer is removed, makes materials based on it promising in scaffold technologies.

Grafting of Methyl Methacrylate onto Gelatin Initiated by Tri-Butylborane-2,5-Di-Tert-Butyl-p-Benzoquinone System.

Graft gelatin and poly(methyl methacrylate) copolymers were synthesized in the presence of the tributylborane-2,5-di-tert-butyl-p-benzoquinone (2,5-DTBQ) system. The molecular weight parameters and morphology of the polymer indicate that it has a cross-linked structure. Obtained data confirm the simultaneous formation of a copolymer in two ways: "grafting from" and "grafting to". It leads to the cross-linked structure of a copolymer. This structure was not obtained for copolymers synthesized in the presence of other initiating systems: azobisisobutyronitrile; tributylborane; azobisisobutyronitrile and tributylborane; azobisisobutyronitrile, tributylborane, and 2,5-di-tert-butyl-p-benzoquinone. In these cases, the possibility of the formation of the copolymer, simultaneously in two ways, was excluded. Graft gelatin and poly(methyl methacrylate) copolymers synthesized in the presence of the tributylborane-2,5-di-tert-butyl-p-benzoquinone system are promising in terms of their use in scaffold technologies due to the three-dimensional mesh structure, providing a high regenerative potential of materials.