A Nonflammable High-Voltage 4.7 V Anode-Free Lithium Battery.

Anode-free lithium-metal batteries employ in situ lithium-plated current collectors as negative electrodes to afford optimal mass and volumetric energy densities. The main challenges to such batteries include their poor cycling stability and the safety issues of the flammable organic electrolytes. Here, a high-voltage 4.7 V anode-free lithium-metal battery is reported, which uses a Cu foil coated with a layer (≈950 nm) of silicon-polyacrylonitrile (Si-PAN, 25.5 µg cm-2 ) as the negative electrode, a high-voltage cobalt-free LiNi0.5 Mn1.5 O4 (LNMO) as the positive electrode and a safe, nonflammable ionic liquid electrolyte composed of 4.5 m lithium bis(fluorosulfonyl)imide (LiFSI) salt in N-methyl-N-propyl pyrrolidiniumbis(fluorosulfonyl)imide (Py13 FSI) with 1 wt% lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) as additive. The Si-PAN coating is found to seed the growth of lithium during charging, and reversibly expand/shrink during lithium plating/stripping over battery cycling. The wide-voltage-window electrolyte containing a high concentration of FSI- and TFSI- facilitates the formation of stable solid-electrolyte interphase, affording a 4.7 V anode-free Cu@Si-PAN/LiNi0.5 Mn1.5 O4 battery with a reversible specific capacity of ≈120 mAh g-1 and high cycling stability (80% capacity retention after 120 cycles). These results represent the first anode-free Li battery with a high 4.7 V discharge voltage and high safety.

Rechargeable Na/Cl2 and Li/Cl2 batteries.

Lithium-ion batteries (LIBs) are widely used in applications ranging from electric vehicles to wearable devices. Before the invention of secondary LIBs, the primary lithium-thionyl chloride (Li-SOCl2) battery was developed in the 1970s using SOCl2 as the catholyte, lithium metal as the anode and amorphous carbon as the cathode1-7. This battery discharges by lithium oxidation and catholyte reduction to sulfur, sulfur dioxide and lithium chloride, is well known for its high energy density and is widely used in real-world applications; however, it has not been made rechargeable since its invention8-13. Here we show that with a highly microporous carbon positive electrode, a starting electrolyte composed of aluminium chloride in SOCl2 with fluoride-based additives, and either sodium or lithium as the negative electrode, we can produce a rechargeable Na/Cl2 or Li/Cl2 battery operating via redox between mainly Cl2/Cl- in the micropores of carbon and Na/Na+ or Li/Li+ redox on the sodium or lithium metal. The reversible Cl2/NaCl or Cl2/LiCl redox in the microporous carbon affords rechargeability at the positive electrode side and the thin alkali-fluoride-doped alkali-chloride solid electrolyte interface stabilizes the negative electrode, both are critical to secondary alkali-metal/Cl2 batteries.

A high-performance potassium metal battery using safe ionic liquid electrolyte.

Potassium secondary batteries are contenders of next-generation energy storage devices owing to the much higher abundance of potassium than lithium. However, safety issues and poor cycle life of K metal battery have been key bottlenecks. Here we report an ionic liquid electrolyte comprising 1-ethyl-3-methylimidazolium chloride/AlCl3/KCl/potassium bis(fluorosulfonyl) imide for safe and high-performance batteries. The electrolyte is nonflammable and exhibits a high ionic conductivity of 13.1 mS cm-1 at room temperature. A 3.6-V battery with K anode and Prussian blue/reduced graphene oxide cathode delivers a high energy and power density of 381 and 1,350 W kg-1, respectively. The battery shows an excellent cycling stability over 820 cycles, retaining ∼89% of the original capacity with high Coulombic efficiencies of ∼99.9%. High cyclability is also achieved at elevated temperatures up to 60 °C. Uniquely, robust K, Al, F, and Cl-containing passivating interphases are afforded with this electrolyte, which is key to superior battery cycling performances.

High-Safety and High-Energy-Density Lithium Metal Batteries in a Novel Ionic-Liquid Electrolyte.

Rechargeable lithium metal batteries are next generation energy storage devices with high energy density, but face challenges in achieving high energy density, high safety, and long cycle life. Here, lithium metal batteries in a novel nonflammable ionic-liquid (IL) electrolyte composed of 1-ethyl-3-methylimidazolium (EMIm) cations and high-concentration bis(fluorosulfonyl)imide (FSI) anions, with sodium bis(trifluoromethanesulfonyl)imide (NaTFSI) as a key additive are reported. The Na ion participates in the formation of hybrid passivation interphases and contributes to dendrite-free Li deposition and reversible cathode electrochemistry. The electrolyte of low viscosity allows practically useful cathode mass loading up to ≈16 mg cm-2 . Li anodes paired with lithium cobalt oxide (LiCoO2 ) and lithium nickel cobalt manganese oxide (LiNi0.8 Co0.1 Mn0.1 O2 , NCM 811) cathodes exhibit 99.6-99.9% Coulombic efficiencies, high discharge voltages up to 4.4 V, high specific capacity and energy density up to ≈199 mAh g-1 and ≈765 Wh kg-1 respectively, with impressive cycling performances over up to 1200 cycles. Highly stable passivation interphases formed on both electrodes in the novel IL electrolyte are the key to highly reversible lithium metal batteries, especially for Li-NMC 811 full batteries.