MDP is effective for removing residual polycarboxylate temporary cement as an adhesion inhibitor.

The effect of cleaner containing 10-methacryloyloxydecyl dihydrogen phosphate (MDP) for removing temporary cement remnants on dentin surface was evaluated. Flat dentin surfaces were wet-polished (Co) and HY-BOND temporary cement hard (Shofu) was applied to the surface. This temporary cement was removed using an air-scaler (Sc), brush (Br), or phosphoric acid and NaOCl (NC). A prototype cleaner containing MDP (Kuraray Noritake Dental, Tokyo, Japan) was used with agitation mode (MC+AG). KATANA Avencia block (Kuraray Noritake Dental) was luted with SA Cement Plus Automix (Kuraray Noritake Dental). Co showed significantly higher bond strength than Sc or Br (p<0.001 each). Bond strengths with NC (p=0.99) and MC+AG (p=0.38) did not differ significantly from that with Co. Transmission electron microscopy revealed sufficient interaction of MC+AG. Cleaner containing MDP can effectively remove temporary cement by agitation, and can be expected to improve the chemical bonding ability by binding more MDP to dentin.

Adhesion procedures for CAD/CAM indirect resin composite block: A new resin primer versus a conventional silanizing agent.

PURPOSE: The purpose of this study was to evaluate the effectiveness of both a resin primer containing methyl methacrylate (MMA) and a silanizing agent on bonding to indirect resin composite blocks, using two types of build-up hybrid resin composites. METHODS: SHOFU BLOCK HC (Shofu) specimens were blasted with alumina, after which one of two surface treatments was applied: CERA RESIN BOND (Shofu, the Silane group) or HC primer (Shofu, the MMA group). Resin composites made using either Solidex Hardura (SDH, Shofu) or Ceramage Duo (CMD, Shofu) were built up and micro-tensile bond strength (µTBS) values were measured after storage in water for either 24h or 6 months (n=24 per group). The fracture surfaces after µTBS measurements and the resin block/build-up resin interfaces were observed by scanning electron microscopy (SEM). RESULTS: The bond strength of the Silane/SDH group significantly decreased after 6 months (p<0.001), whereas in the MMA group there was no significant loss after 24h or 6 months (p=0.99). In the CMD group, the bond strength after 6 months was significantly lowered in both the Silane group (p<0.001) and the MMA group (p<0.001), but the latter still showed greater adhesion. SEM images demonstrated that the matrix resin was partially destroyed at the fracture surfaces of the MMA group and fracture surface unevenness was observed. CONCLUSIONS: A primer containing MMA produced stronger bonding to CAD/CAM resin even after long-term aging compared to a silane treatment.