ABSTRACT
Both conductivity and mobility are essential to charge transfer by carrier transport layers (CTLs) in perovskite solar cells (PSCs). The defects derived from generally used ionic doping method lead to the degradation of carrier mobility and parasite recombinations. In this work, a novel molecular doping of NiOx hole transport layer (HTL) is realized successfully by 2,2'-(perfluoronaphthalene-2,6-diylidene)dimalononitrile (F6TCNNQ). Determined by X-ray photoelectron spectroscopy and ultraviolet photoelectron spectroscopy, the Fermi level (EF ) of NiOx HTLs is increased from -4.63 to -5.07 eV and valence band maximum (VBM)-EF declines from 0.58 to 0.29 eV after F6TCNNQ doping. The energy level offset between the VBMs of NiOx and perovskites declines from 0.18 to 0.04 eV. Combining with first-principle calculations, electrostatic force microscopy is applied for the first time to verify direct electron transfer from NiOx to F6TCNNQ. The average power conversion efficiency of CsFAMA mixed cation PSCs is boosted by ≈8% depending on F6TCNNQ-doped NiOx HTLs. Strikingly, the champion cell conversion efficiency of CsFAMA mixed cations and MAPbI3 -based devices gets to 20.86% and 19.75%, respectively. Different from passivation effect, the results offer an extremely promising molecular doping method for inorganic CTLs in PSCs. This methodology definitely paves a novel way to modulate the doping in hybrid electronics more than perovskite and organic solar cells.
ABSTRACT
We examined different encapsulation strategies for perovskite solar cells by testing the device stability under continuous illumination, elevated temperature (85 °C) and ambient humidity of 65 %. The effects of the use of different epoxies, protective layers and the presence of desiccant were investigated. The best stability (retention of â¼80 % of initial efficiency on average after 48â h) was obtained for devices protected by a SiO2 film and encapsulated with a UV-curable epoxy including a desiccant sheet. However, the stability of ZnO-based cells encapsulated by the same method was found to be inferior to that of TiO2 -based cells. Finally, outdoor performance tests were performed for TiO2 -based cells (30-90 % ambient humidity). All the stability tests were performed following the established international summit on organic photovoltaic stability (ISOS) protocols for organic solar cell testing (ISOS-L2 and ISOS-O1).