ABSTRACT
A CoCrCuFeNi high-entropy alloy was successfully welded in this study using fiber laser welding. The effects of the welding parameters on the microstructure and mechanical properties were studied. Three zones were formed: the fusion zone, partial melting zone, and base metal. The base metal exhibited a typical dendrite structure, and the Cu element segregated in the interdendrite. The fusion zone consisted of fine equiaxed crystals and columnar crystals with the same crystalline structure as the base metal. The fusion zone exhibited minimal compositional microsegregation after laser welding. Electron backscatter diffraction results showed that the low-angle grain boundary fraction in the fusion zone increased. Furthermore, some dislocations and dislocation pile-ups were present in the fusion zone, and the densities of the dislocations and dislocation pile-ups were higher than those of the base metal. The hardness of the fusion zone was considerably higher than that of the base metal, while the ultimate tensile strength and elongation values were lower than those of the base metal for all conditions. The ultimate tensile strength and the elongation increased gradually and then decreased with increasing laser power. The maximum ultimate tensile strength exceeded that of the base metal by 90%.
ABSTRACT
Ni-CeO2/SBA-15-V catalyst was prepared by the impregnation method with vacuum thermal treatment and used for CO2 methanation reaction. Compared with Ni-CeO2/SBA-15-air catalyst with thermal treatment in air, the reduced Ni-CeO2/SBA-15-V catalyst with vacuum thermal treatment exhibited higher Ni dispersion and smaller Ni particle size. In CO2 methanation reaction, the Ni-CeO2/SBA-15-V catalyst was more active and selective than the Ni-CeO2/SBA-15-air catalyst. The good activity and selectivity of Ni-CeO2/SBA-15-V catalyst should be due to highly dispersed Ni in contact with small CeO2 particles.