Surface engineering of nanoporous substrate for solid oxide fuel cells with atomic layer-deposited electrolyte.

Solid oxide fuel cells with atomic layer-deposited thin film electrolytes supported on anodic aluminum oxide (AAO) are electrochemically characterized with varying thickness of bottom electrode catalyst (BEC); BECs which are 0.5 and 4 times thicker than the size of AAO pores are tested. The thicker BEC ensures far more active mass transport on the BEC side and resultantly the thicker BEC cell generates ≈11 times higher peak power density than the thinner BEC cell at 500 °C.

Intermediate-Temperature Solid-Oxide Fuel Cells with a Gadolinium-Doped Ceria Anodic Functional Layer Deposited via Radio-Frequency Sputtering.

We investigated the effects of the insertion of a gadolinium-doped ceria (GDC) anodic functional layer (AFL) on the electrochemical performance of intermediate-temperature solid-oxide fuel cells (SOFCs). Fully stabilized yttria-stabilized zirconia (YSZ) was used as an oxygen-ion-conducting and support material. Nickel-Samaria-doped ceriathin film was used as an anode material, while screen-printed lanthanum strontium magnetite served as a cathode material. In order to enhance the interfacial reaction on the anode side, a GDC-AFL with a thickness of about 140 nm, deposited via radio-frequency sputtering, was inserted into the anode-electrolyte interface. SOFCs with and without a GDC-AFL were electrochemically characterized. In an intermediate temperature range of about 700 - 800 degrees C, the application of the GDC-AFL led to an increase in the peak power density of approximately 16%.