ABSTRACT
To solve the problem of water pollution, using environment friendly and cost effective method in short time is the need of hour. In this work, chromium (Cr) and nitrogen (N) co-doped TiO2 nanoparticles were synthesized and were used for the photocatalytic degradation of dyes under visible light. The synergistic effect of metal and non-metal co-dopants added would result in appropriate reduction of band gap {from 3.2 eV of TiO2 to 2.67 eV}, decrease in recombination rate of charge carriers by trapping electrons and holes, and in better light harvesting capacity. Nanoparticles were synthesized by sol-gel method and characterized using ultraviolet-visible (UV-VIS) spectroscopy, fourier transform infrared (FTIR) spectroscopy, atomic force microscopy (AFM), zeta potential, X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) analysis, field emission scanning electron microscopy (FE-SEM), and RAMAN spectroscopy. Eosin yellow (EY) and rose bengal (RB) were subjected to photocatalytic degradation under solar light to check the photocatalytic activity of the synthesized nanoparticles. Effects of dye concentration, the concentration of nanoparticles, time, and pH were investigated to optimize the parameters. The results obtained were remarkable for 20 ppm EY solution took 10 min using 1 gL-1 NPs at pH 3 and 10 ppm RB solution took 5 min using 0.75 gL-1 NPs at pH 5.78 (original pH) for complete degradation. Kinetics studies were also performed and both dyes followed pseudo-second-order kinetics with R2 values 0.99312 and 0.99712 for EY and RB, respectively. The study of degraded products was conducted using high-performance liquid chromatography (HPLC) hyphenated with electron spray ionization mass spectroscopy (ESI-MS) (LC-MS) and possible degradation pathways were made for both dyes. A reusability test was also performed showing the efficiency of the particles was up to 88% after 3 cycles of use. These notable results can be attributed to the efficient removal of organic pollutants using the proposed dopants in this study.
Subject(s)
Nanoparticles , Rose Bengal , Eosine Yellowish-(YS) , Chromium , Light , Titanium/chemistry , Nanoparticles/chemistry , Benzopyrans , Coloring Agents , CatalysisABSTRACT
The purpose to conduct this research work is to study the effect of photocatalytic degradation by developing cost-effective and eco-friendly nitrogen and tungsten (metal/non-metal) co-doped titania (TiO2). The inherent characteristics of synthesized nanoparticles (NPs) were analyzed by Fourier transform infra-red spectroscopy (FT-IR), ultra-violet visible (UV-Vis) spectroscopy, Raman spectroscopy, Field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS), X-ray diffraction (XRD) spectrometry, and atomic force microscopy (AFM). Co-doping of metal and non-metal has intensified the photocatalysis trait of TiO2 nanoparticles in an aqueous medium. This co-doping of transition metal ions and modification of nitrogen extended the absorption into the visible region subsequently restraining the recombination of electrons/holes pair. The stronger light absorption in the visible region was required for the higher activity of photodegradation of dye under visible light illumination to confine bandgap energy which results in accelerating the rate of photodegradation. After efficient doping, the bandgap of titania reduced to 2.38 eV and caused the photodegradation of malachite green in visible light. The results of photocatalytic degradation were confirmed by using UV/Vis. spectroscopy and high-performance liquid chromatography coupled with a mass spectrophotometer (HPLC-ESI-MS) was used for the analysis of intermediates formed during photocatalytic utility of the work.
ABSTRACT
A memristor is a fundamental electronic device that operates like a biological synapse and is considered as the solution of classical von Neumann computers. Here, a fully printed and flexible memristor is fabricated by depositing a thin film of metal-non-metal (chromium-nitrogen)-doped titanium dioxide (TiO2). The resulting device exhibited enhanced performance with self-rectifying and forming free bipolar switching behavior. Doping was performed to bring stability in the performance of the memristor by controlling the defects and impurity levels. The forming free memristor exhibited characteristic behavior of bipolar resistive switching with a high on/off ratio (2.5 × 103), high endurance (500 cycles), long retention time (5 × 103 s) and low operating voltage (±1 V). Doping the thin film of TiO2 with metal-non-metal had a significant effect on the switching properties and conduction mechanism as it directly affected the energy bandgap by lowering it from 3.2 eV to 2.76 eV. Doping enhanced the mobility of charge carriers and eased the process of filament formation by suppressing its randomness between electrodes under the applied electric field. Furthermore, metal-non-metal-doped TiO2 thin film exhibited less switching current and improved non-linearity by controlling the surface defects.